The present invention discloses a zinc powder for improving the two adhesion of water based epoxy zinc rich coatings, mainly made of raw materials with the following mass ratio: modified amine curing agent 10~15, PM 5~10, dispersant 1~3, wetting agent 0.5 ~ 1, silane coupling agent 2~4, anticorrosive agent 1~2 and zinc powder 70~80. The zinc powder is silane coupling agent, which is dispersed and wetted with zinc powder in advance. It has very good wet adhesion and can greatly enhance the adhesion force of the coating two times. The invention also discloses the coating process of the zinc powder used for improving the two adhesion of waterborne epoxy zinc rich coatings.
【技术实现步骤摘要】
一种用于提高水性环氧富锌涂料二次附着力的锌粉浆及其包覆工艺
本专利技术属于粉末涂料
，具体涉及一种用于提高水性环氧富锌涂料二次附着力的锌粉浆及其包覆工艺。
技术介绍
水性环氧富锌涂料以环氧树脂作为主要成膜物质，具有漆膜附着力良好、耐腐蚀性能极佳、施工方便、与面漆配套相容性好等特点，被广泛应用于海上采油平台、码头、管道、桥梁、集装箱等工业重防腐领域，其他防腐蚀体系的耐腐蚀性能与之无法相比。公开号CN102863874A的中国专利公开的水性环氧富锌底漆及其制备方法将成膜助剂、防沉剂一、防沉剂二、胺类环氧固化剂、分散剂、消泡剂、填料和锌粉作为主剂，将环氧乳液、防沉剂三、防闪锈剂和去离子水作为固化剂，按比例配套使用制得水性环氧富锌底漆；还有公开号CN104774526A的中国专利公开的室温固化双组份水性环氧富锌底漆将环氧树脂、环氧稀释剂、助溶剂、有机膨润土、锌粉和云母氧化铁作为A组分，将水性环氧固化剂、水、润湿剂作为乙组分。两份专利公开的水性环氧富锌涂料产品均具有优良耐腐蚀性能、安全、环保，但是对于涂膜在耐盐雾测试后的二次附着力都未进行检测。目前，市售水性环氧富锌涂...
【技术保护点】
一种用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是主要由以下质量份配比的原料制成：
【技术特征摘要】
1.一种用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是主要由以下质量份配比的原料制成：2.根据权利要求1所述的用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是：所述的改性胺固化剂为不含水的聚酰胺和改性脂肪胺中的一种或几种的混合物。3.根据权利要求1所述的用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是：所述的PM为含水率达到氨酯级的丙二醇甲醚溶剂。4.根据权利要求1所述的用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是：所述的分散剂为高分子型分散剂、非离子型分散剂和磷酸酯型分散剂中的一种或几种的混合物。5.根据权利要求1所述的用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是：所述的润湿剂为有机硅类润湿剂、炔二醇类润湿剂、丙烯酸类润湿剂和氟类润湿剂中的一种或几种的混合物。6.根据权利要求1所述的用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是：所述的硅烷偶联剂为带有氨基基团的硅烷偶联剂、带有环氧基团的硅烷偶联剂和带有乙烯基团的硅烷偶联剂中的一种或几种的混合物。7.根据权利要求1所述的用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是：所述的防沉剂为膨润土、聚脲和气相二氧化硅中的一种或几种的混合物。8.根据权利要求1所述的用于提高水性环氧富锌涂料二次附着力的锌粉浆，其特征是：所述的锌粉为加工成涂料使用的不同粒径的锌粉中的一种或几种的混合物。9.权利要求1-8任一项所述的用于提...
【专利技术属性】
技术研发人员：禹汉文，姚煌，王从国，
申请(专利权)人：广州擎天材料科技有限公司，
类型：发明
国别省市：广东,44