The invention discloses a kind of shock resistant polyethylene plastic for automobile bumper, which consists of 80 polyethylene, 120 copies of polyethylene, 20 chlorosinated polyethylene, three ethylene propylene rubber 8, 8 parts of ethylene propylene rubber, 4 crosslinking agent, 4 polyacrylonitrile carbon fiber 4, 8 copies of polyacrylonitrile fiber, 6 carbon nanotube, glass fiber Dimension 6, 12, methyl silicone oil 2, 4, disproportionated rosin 2, 4, antioxidant 3, 5. The invention has high hardness, good flexibility, toughness and glossiness, excellent impact resistance, high pressure bearing capacity, avoiding the phenomenon of bending when the invention is impacted, excellent heat resistance and aging resistance, high elongation at break, suitable for automobile plastic bumper, and can effectively reduce vehicle risk.
【技术实现步骤摘要】
一种汽车保险杠用耐冲击聚乙烯塑料
本专利技术涉及汽车保险杠
，尤其涉及一种汽车保险杠用耐冲击聚乙烯塑料。
技术介绍
聚乙烯易成型加工、可回收利用等优点，在汽车上的应用不断增大，特别是应用于制备汽车保险杠，是汽车用塑料中用量最大、发展速度最快的塑料品种。但是聚乙烯的低温脆性差、耐冲击性能差的缺点，因此，用于汽车保险杠时需要对其改性。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种汽车保险杠用耐冲击聚乙烯塑料，硬度高，具有较好的柔韧度、韧性及光泽度，抗冲击性能极好，承压能力极高，避免本专利技术受到冲击时弯折的现象，而且耐热、耐老化性能极为优异，断裂伸长率高，适用于汽车塑料保险杠，可有效降低乘车危险。本专利技术提出的一种汽车保险杠用耐冲击聚乙烯塑料，其原料按重量份包括：聚乙烯80-120份，氯磺化聚乙烯10-20份，三元乙丙橡胶8-16份，交联剂4-8份，聚丙烯腈基碳纤维4-8份，碳纳米管6-10份，纳米膨润土4-10份，玻璃纤维6-12份，甲基硅油2-4份，歧化松香2-4份，防老剂3-5份。优选地，交联剂按重量份包括：叔丁基过氧化氢2-4份，氧化钇0...
【技术保护点】
一种汽车保险杠用耐冲击聚乙烯塑料，其特征在于，其原料按重量份包括：聚乙烯80‑120份，氯磺化聚乙烯10‑20份，三元乙丙橡胶8‑16份，交联剂4‑8份，聚丙烯腈基碳纤维4‑8份，碳纳米管6‑10份，纳米膨润土4‑10份，玻璃纤维6‑12份，甲基硅油2‑4份，歧化松香2‑4份，防老剂3‑5份。
【技术特征摘要】
1.一种汽车保险杠用耐冲击聚乙烯塑料，其特征在于，其原料按重量份包括：聚乙烯80-120份，氯磺化聚乙烯10-20份，三元乙丙橡胶8-16份，交联剂4-8份，聚丙烯腈基碳纤维4-8份，碳纳米管6-10份，纳米膨润土4-10份，玻璃纤维6-12份，甲基硅油2-4份，歧化松香2-4份，防老剂3-5份。2....
【专利技术属性】
技术研发人员：刘仕明，
申请(专利权)人：全椒祥瑞塑胶有限公司，
类型：发明
国别省市：安徽,34