The invention discloses an environmentally friendly regenerative rubber preparation method, which comprises the following steps: (1) mixing coal tar, activator, rosin and stearic acid; (2) mixing waste rubber powder, ammonium phosphate and alumina; (3) mixing, heating and stirring; and adding pentaerythritol and water in turn and heating up. Strong mixing; (4) the material can be extruded in a twin screw extruder. The preparation method of the invention has the advantages of simple operation, low cost, no waste water and waste gas, little pollution to the environment, high strength and good toughness of the regenerated rubber, and can meet the demand of industrial production, and has a broad market prospect.
【技术实现步骤摘要】
一种环境友好的再生橡胶制备方法
本专利技术涉及一种橡胶制备方法，特别涉及一种环境友好的再生橡胶制备方法。
技术介绍
再生胶能部分地代替生胶用于橡胶制品，以节约生胶及炭黑也有利于改善加工性能及橡胶制品的某些性能。再生过程是废胶在增塑剂（软化剂和活化剂）、氧、热和机械剪切的综合作用下使硫化橡胶的部分分子链和交联点断裂的过程。橡胶再生的方法一般分为物理法、化学法也其他方法，而在橡胶再生过程中，尤其是化学法再生橡胶过程中，往往会产生污染性的气体、废水等环境污染物，而在橡胶应用后由于其不易降解也同样产生了环境问题，同时目前的再生橡胶产品性能欠佳，强度低，弹性差，易磨损、老化，难以满足工业上优质产品对橡胶原料性能的需求。
技术实现思路
技术问题：本专利技术所要解决的技术问题是针对现有技术中制备再生橡胶能耗大，有废水、废气产生，污染环境，并且制得的再生橡胶性能欠佳，强度低的不足，提供一种环境友好的再生橡胶制备方法，其操作简便，生产条件温和，能够有效节约能源，无废水、废气产生，对环境污染小，且制得的再生橡胶具有较佳的强度、韧性等性能，能够满足工业上对优质原料的需求。技术方案：为实现上...
【技术保护点】
一种环境友好的再生橡胶制备方法，其特征在于，包括以下步骤：步骤一，将以重量份计的煤焦油16~23份，活化剂0.3~0.6份，松香0.3~0.8份，硬脂酸0.4~0.8份加入到混合搅拌机中加热混合，于70~90℃搅拌20~30分钟，得物料A，将物料A的温度保持在70~90℃；步骤二，将以重量份计的废旧橡胶粉100份，三聚磷酸铵0.5~0.9份，氧化铝0.5~1.0份加入反应釜内，充分搅拌，混合均匀，得到物料B；步骤三，搅拌下，向物料B中加入物料A，加热至80~100℃，搅拌0.5~1小时；再依次加入季戊四醇0.4~0.8份，水0.2~0.4份，升温至120~150℃，强力搅拌...
【技术特征摘要】
1.一种环境友好的再生橡胶制备方法，其特征在于，包括以下步骤：步骤一，将以重量份计的煤焦油16~23份，活化剂0.3~0.6份，松香0.3~0.8份，硬脂酸0.4~0.8份加入到混合搅拌机中加热混合，于70~90℃搅拌20~30分钟，得物料A，将物料A的温度保持在70~90℃；步骤二，将以重量份计的废旧橡胶粉100份，三聚磷酸铵0.5~0.9份，氧化铝0.5~1.0份加入反应釜内，充分搅拌，混合均匀，得到物料B；步骤三，搅拌下，向物料B中加入物料A，加热至80~100℃，搅拌0.5~1小时；再依次加入季戊四醇0.4~0.8份，水0.2~0.4份，升温至120~150℃，强力搅拌1~1.5小时；得到物料C；步骤四，将...
【专利技术属性】
技术研发人员：陈立奇，
申请(专利权)人：江苏华兴橡胶科技有限公司，
类型：发明
国别省市：江苏,32