The invention belongs to the technical field of refractory material, in particular to a tin trough ceiling brick for aluminic acid calcium glass kiln and the preparation method. The calcium aluminate glass furnace tin bath ceiling brick raw material: 6 aluminum acid calcium compact 3mm 10 25%; 3 1mm dense calcium aluminate 15 30%; 1 0.1mm compact aluminum acid calcium 20 40%; pure calcium aluminate cement powder 5 20%; alpha alumina 5 20% 0.2 3% siliceous compound powder. The preparation of calcium aluminate glass furnace tin bath ceiling brick, uniform internal structure, low porosity, low thermal conductivity, high temperature creep rate is low, and the alkali metal oxide Na2O in the use of temperature without chemical reaction, solve the silicon aluminum acid ceiling brick easily peel off, causing glass defect the problem, reduce the heat loss in the tin groove, improve the service life of the tin bath ceiling brick; the preparation method, reasonable and easy.
【技术实现步骤摘要】
铝酸钙质玻璃窑炉锡槽吊顶砖及其制备方法
本专利技术属于耐火材料
，具体涉及一种铝酸钙质玻璃窑炉锡槽吊顶砖及其制备方法。
技术介绍
锡槽是浮法平板玻璃生产线的关键设备，其主要由锡槽底砖和锡槽吊顶砖组成。目前，锡槽吊顶砖主要采用组合式结构，市场上多数材质采用硅酸铝质制作而成。在其使用过程中，由于玻璃带在锡槽内成型时其玻璃成分中所含的Na2O有百分之五左右的量挥发，使其与盖顶硅酸铝质耐火材料中的硅、铝反应形成玻璃相，随着釉层的不断增厚，在其自身重力作用下脱落到玻璃板上从而使玻璃产生缺陷。中国专利CN104326755A公开了一种低导热莫来石锡槽组合顶盖砖，采用低导热的莫来石粗颗粒和细颗粒为骨料，采用铝酸钙、氧化铝粉、硅微粉等为粘结剂，经振动成型，养护后烘干、烧成而得，制得的锡槽组合顶盖砖具有低导热、抗热震性好、高温强度高的特点。但是，其采用的颗粒和细粉多数为硅、铝系原料，长期使用过程中难免和玻璃蒸发出的碱金属氧化物Na2O产生反应，导致最终的脱落造成玻璃缺陷的风险。
技术实现思路
针对现有技术的不足，本专利技术的目的是提供一种铝酸钙质玻璃窑炉锡槽吊顶砖，内部结构均匀，...
【技术保护点】
一种铝酸钙质玻璃窑炉锡槽吊顶砖，其特征在于：由如下重量百分数的原料制成：
【技术特征摘要】
1.一种铝酸钙质玻璃窑炉锡槽吊顶砖，其特征在于：由如下重量百分数的原料制成：2.根据权利要求1所述的铝酸钙质玻璃窑炉锡槽吊顶砖，其特征在于：所述的致密铝酸钙为气孔率小于3％的铝酸钙。3.根据权利要求1所述的铝酸钙质玻璃窑炉锡槽吊顶砖，其特征在于：所述的纯铝酸钙水泥粉、α-氧化铝粉与硅质化合物粉的粒径均＜0.088mm。4.根据权利要求1所述的铝酸钙质玻璃窑炉锡槽吊顶砖，其特征在于：所述的硅质化合物为硅微粉、粘土、石英或硅灰石中的一种。5.根据权利要求1所述的铝酸钙质玻璃窑炉锡槽吊顶砖，其特征在于：所述的铝酸钙质玻璃窑炉锡槽吊顶砖的气孔率为13-20％。6.根据权利要求1所述的铝酸钙质玻璃窑炉锡槽吊顶砖，其特征在于：所述的铝酸钙质玻璃窑炉锡槽吊顶砖的XRD矿物相组成包括：...
【专利技术属性】
技术研发人员：孙文礼，张晓峰，李玉强，张瑛，李志军，
申请(专利权)人：淄博工陶耐火材料有限公司，
类型：发明
国别省市：山东,37