The invention relates to a two silicone softener, according to weight, which comprises the following components: two 30~80 methyl silicone oil viscosity is less than 18cs, 10~30 of sodium stearate, trimethylamine 30~80, double sixteen alkyl two methyl ammonium methyl sulfate 10~30, sodium silicate 20~60, six methyl siloxane two 3 6, PEG 120 two stearic acid ester 5~20, and n-butanol 100~300, deionized water, 600 800. The present invention adopts two components of methyl silicone oil and n-butanol together with stearic acid, and does not need to heat up to 70 degrees or more to prepare stearic acid in preparation process, so that it is easier to prepare. And the softener of the invention has good effect and does not damage the surface of the fabric.
【技术实现步骤摘要】
二甲基硅油柔软剂
本专利技术涉及一种二甲基硅油柔软剂，属于纺织助剂
技术介绍
纺织物在后整理过程中，需要使用柔软剂对织物进行柔软蓬松处理，以改善织物的触感与观感，现有技术采用氨基硅油作为柔软剂对织物进行柔软蓬松整理，由于氨基硅油柔软剂整理的织物黄变严重、吸湿透气性差、蓬松感欠佳，因此，现有技术存在黄变严重、吸湿透气性差、蓬松感欠佳的问题与不足。因此有必要设计一种二甲基硅油柔软剂，以克服上述问题。
技术实现思路
本专利技术的目的在于克服现有技术之缺陷，提供了一种二甲基硅油柔软剂，该柔软剂使用效果良好、不损伤织物表面。本专利技术是这样实现的：本专利技术提供一种二甲基硅油柔软剂，按照重量份数计，其组分包括：粘度小于18cs的二甲基硅油30~80份，硬脂酸钠10~30份，三甲胺30~80份，双十六烷基二甲基铵甲基硫酸盐10~30份，硅酸钠20~60份，六甲基二硅氧烷3-6份，PEG-120二硬脂酸酯5~20份，以及正丁醇100~300份，去离子水600-800份。进一步地，按照重量份数计，其组分包括：粘度小于18cs的二甲基硅油50~80份，硬脂酸钠20~30份，三...
【技术保护点】
一种二甲基硅油柔软剂，其特征在于，按照重量份数计，其组分包括：粘度小于18cs的二甲基硅油30~80份，硬脂酸钠10~30份，三甲胺30~80份，双十六烷基二甲基铵甲基硫酸盐10~30份，硅酸钠20~60份，六甲基二硅氧烷3‑6份，PEG‑120二硬脂酸酯5~20份，以及正丁醇100~300份，去离子水600‑800份。
【技术特征摘要】
1.一种二甲基硅油柔软剂，其特征在于，按照重量份数计，其组分包括：粘度小于18cs的二甲基硅油30~80份，硬脂酸钠10~30份，三甲胺30~80份，双十六烷基二甲基铵甲基硫酸盐10~30份，硅酸钠20~60份，六甲基二硅氧烷3-6份，PEG-120二硬脂酸酯5~20份，以及正丁醇100~300份，去离子水600-800份。2.如权利要求1所述的二甲基硅油柔软剂，其特征在于：按照重量份数计，其组分包括：粘度小于18cs的二甲基硅油50~80份，硬脂酸钠20~30份，三甲胺60~80份，双十六烷基二甲基铵甲基硫酸盐20~30份，硅酸钠40~60份，六甲基二硅氧烷5份，PEG-120二硬脂酸酯10~20份，以及正丁醇200~300份，去离子水700-800份。3.如权利要求2所述的二甲基硅油柔软剂，其特征在于：按照重量份数计，其组分包括：粘度小于18cs的二甲基硅油60~80份，...