The invention relates to a preparation method of a copper matrix composite material. The method uses copper powder and zirconium carbide as raw materials, ball milling is used for ball milling, raw materials are zirconium carbide balls, and high purity argon gas is sealed in ball milling tank during ball milling. After ball milling, the mixed powder is put into the graphite mold, and the sintering is made using the vacuum hot pressing furnace. At the highest sintering temperature, the constant temperature is maintained and the pressure is applied. After the end of the sintering, the material is the copper based composite. The method is simple, and the copper matrix composite has excellent wear resistance and easy processing performance, and is suitable for making components in the environment under impact and easy wearing conditions.
【技术实现步骤摘要】
一种铜基复合材料的制备方法
本专利技术涉及材料合成制备领域，特别涉及一种铜基复合材料的制备方法。技术背景铜材料具有良好的导电、导热和易于加工性能，广泛应用在轴承、衬套、齿轮、接头和摩擦等组件上。然而，由于纯铜材料强度低、耐磨性差，导致寿命较短，使用范围受到限制。在一些特定领域，需要在保留纯铜材料的金属特性的同时提高其力学性能和机械性能。碳化锆是一种具有金属属性的高硬材料，电导率可达2.3×104S/cm，导电能力与金属相当，作为强化第二相在改善金属材料力学性能方面具有较好的应用前景。但现在大部分技术在制备过程需在氢气氛中进行，危险性高，工艺复杂，控制参数较多，需要精确控制反应温度，难以保证产品质量。
技术实现思路
基于此，本专利技术公开了一种统计复合材料的制备方法，所述方法包括以下步骤：S100、将混合粉体放入球磨罐中加入球磨介质进行球磨；S200、将球磨后的混合粉体放入石墨模具中，然后一同放置在真空热压炉中进行烧结；S300、烧结结束后卸压，随炉冷却至室温，所制备的材料即为铜基复合材料。本专利技术所公开的方法简便，所需控制的工艺参数较少，克服了其他方法工艺参数控...
【技术保护点】
一种铜基复合材料的制备方法，其特征在于，所述方法包括以下步骤：S100、将混合粉体放入球磨罐中加入球磨介质进行球磨；S200、将球磨后的混合粉体放入石墨模具中，然后一同放置在真空热压炉中进行烧结；S300、烧结结束后卸压，随炉冷却至室温，所制备的材料即为铜基复合材料。
【技术特征摘要】
1.一种铜基复合材料的制备方法，其特征在于，所述方法包括以下步骤：S100、将混合粉体放入球磨罐中加入球磨介质进行球磨；S200、将球磨后的混合粉体放入石墨模具中，然后一同放置在真空热压炉中进行烧结；S300、烧结结束后卸压，随炉冷却至室温，所制备的材料即为铜基复合材料。2.根据权利要求1所述的一种铜基复合材料的制备方法，其特征在于：优选的，所述步骤S100中的混合粉体成分为铜粉和碳化锆粉，其中铜粉和碳化锆粉按质量百分比99.5～92.5：0.5～7.5配比。3.根据权利要求2所述的一种铜基复合材料的制备方法，其特征在于：所述铜粉的粒径分布为3～5μm，纯度为99.97％；碳...