扁线的激光焊接方法技术
Laser welding of flat wire
The invention provides a flat wire laser welding method, which makes the side end of the insulating film covers the first and second flat wire respectively the insulation film formed by peeling together each other, and the first and second flat line surface irradiated by a laser beam, which is used for welding side. The method comprises the following steps: the laser welding end in the first flat line, and through annular laser beam irradiation, thus forming a molten pool; end in the first flat line, through the ring increases the irradiation of a laser beam path diameter, so that the molten pool at the side.
【技术实现步骤摘要】
扁线的激光焊接方法
本专利技术涉及一种扁线的激光焊接方法。
技术介绍
电动机用的定子具备定子芯和安装在定子芯的槽中的多个分段线圈。通常，各个分段线圈为覆盖有绝缘膜的扁线。分段线圈的端部彼此通过焊接等而被接合在一起。在日本特开2013-109948中，公开了一种例如被使用在分段线圈中的扁线的激光焊接方法。在日本特开2013-109948中，在分别将覆盖有绝缘膜的一对扁线中的端部的侧面的绝缘膜剥离之后，使该端部的侧面彼此对接在一起，并对扁线的端面照射激光束，从而对端部的侧面彼此进行焊接。关于日本特开2013-109948所公开的扁线的激光焊接方法，专利技术人发现了以下的问题。图16为用于对日本特开2013-109948所公开的激光焊接方法中的问题进行说明的图，并且为接合部的侧视图。如图16所示，在扁线50a中，在绝缘膜51a被剥离了的侧面53a和绝缘膜51a未被剥离的部位之间具有高低差。同样地，在扁线50b中，在绝缘膜51b被剥离了的侧面53b和绝缘膜51b未被剥离的部位之间具有高低差。此外，虽然未图示，但是由于端面54a、54b被切断加工，因此在端面54a，54b中...
【技术保护点】
一种扁线的激光焊接方法，其通过使在覆盖有第一绝缘膜的第一扁线中将第一绝缘膜剥离而形成的第一端部的第一侧面和在覆盖有第二绝缘膜的第二扁线中将第二绝缘膜剥离而形成的第二端部的第二侧面彼此对接在一起，并对所述第一扁线的第一端面和所述第二扁线的第二端面照射激光束，从而对所述第一侧面和所述第二侧面进行焊接，所述激光焊接方法的特征在于，包括如下步骤：在所述第一端面内，通过以环状而照射所述激光束，从而形成熔池；在所述第一端面内，通过以逐渐增大所述环状的轨迹的直径的方式来照射所述激光束，从而使所述熔池到达所述第一侧面及所述第二侧面。
【技术特征摘要】
2016.08.02 JP 2016-1522421.一种扁线的激光焊接方法，其通过使在覆盖有第一绝缘膜的第一扁线中将第一绝缘膜剥离而形成的第一端部的第一侧面和在覆盖有第二绝缘膜的第二扁线中将第二绝缘膜剥离而形成的第二端部的第二侧面彼此对接在一起，并对所述第一扁线的第一端面和所述第二扁线的第二端面照射激光束，从而对所述第一侧面和所述第二侧面进行焊接，所述激光焊接方法的特征在于，包括如下步骤：在所述第一端面内，通过以环状而照射所述激光束，从而形成熔池；在所述第一端面内，通过以逐渐增大所述环状的轨迹的直径的方式来照射所述激光束，从而使所述熔池到达所述第一侧面及所述第二侧面。2.根据权利要求1所述的激光焊接方法，其特征在于，所述环状为圆状或椭圆状。3.根据权利要求1所述的激光焊接方法，其特征在于，所述环状为矩形状。4.根据权利要求1所述的激光焊接方法，其特征在于，所述环状为螺旋状。5.根据权利要求1所述的激光焊接方法，其特征在于，所述环状为椭圆状，且椭圆的长轴与所述第一侧面及第二侧面平行。6.根据权利要求1至5中任一项所述的激光焊接方法，其特征在于，在所述第一端面中，所述激光束仅被照射到所述第一端面中的与所述激光束的照射开始位...