The invention belongs to the field of polymer material synthesis, in particular to a polyether silicone copolymer modified thermoplastic polyurethane elastomer and a preparation method. It is made from raw materials with the following mass fraction: polyester diol 40% to 70%, diisocyanate 15% to 50%, chain extender 3% to 14%, polyether silicone copolymer 1% to 5%, antioxidant 0.1% to 0.5%, light stabilizer 0.1% to 0.1%, catalyst to 0.1%. The invention has excellent hydrolysis resistance, has excellent wear resistance and low cost while solving hydrolysis resistance. The invention also provides its preparation method, and its production process is simple and feasible.
【技术实现步骤摘要】
聚醚硅酮共聚物改性热塑性聚氨酯弹性体及其制备方法
本专利技术属于高分子材料合成领域，具体涉及一种聚醚硅酮共聚物改性热塑性聚氨酯弹性体及其制备方法。
技术介绍
热塑型聚氨酯弹性体(TPU)是一类加热可以塑化、溶剂可以溶解的聚氨酯材料，具有独特的软硬段嵌段共聚物结构，因其同时具有橡胶的弹性和塑料的可加工性，被广泛应用于诸多领域。聚酯型TPU具有优良的机械性能，高强度、高伸长和高弹性，其不足之处在于耐湿热性能不佳，长期在湿热环境中使用可导致TPU链段发生水解而降低其力学性能，大大限制了应用。通常用的耐水解型聚氨酯弹性体多为聚醚型，然而聚醚型聚氨酯弹性体拉伸强度和撕裂性能稍差，无法满足特殊条件下的使用要求，且聚醚型TPU的成本高，限制了其应用领域。对聚酯型聚氨酯弹性体通过添加适量的水解稳定剂，能够提高弹性体的水解稳定性，即使长期在湿热环境中使用也能保持较高的力学性能。通常添加的水解稳定剂为碳化二亚胺类，但目前碳化二亚胺类抗水解剂产品主要依赖进口，价格高昂，使其在产品应用中受到限制。
技术实现思路
针对现有技术的不足，本专利技术的目的是提供一种聚醚硅酮共聚物改性热塑性聚氨酯弹性...
【技术保护点】
一种聚醚硅酮共聚物改性热塑性聚氨酯弹性体，其特征在于：由如下质量分数原料制成：
【技术特征摘要】
1.一种聚醚硅酮共聚物改性热塑性聚氨酯弹性体，其特征在于：由如下质量分数原料制成：2.根据权利要求1所述的聚醚硅酮共聚物改性热塑性聚氨酯弹性体，其特征在于：聚酯型二醇为聚己二酸乙二醇酯二醇、聚己二酸丁二醇酯二醇或聚己二酸己二醇酯二醇中的一种或几种以任意比例混合，聚酯型二醇分子量为1000-4000。3.根据权利要求1所述的聚醚硅酮共聚物改性热塑性聚氨酯弹性体，其特征在于：聚酯型二醇的羟值为28.5-75mgKOH/g。4.根据权利要求1所述的聚醚硅酮共聚物改性热塑性聚氨酯弹性体，其特征在于：二异氰酸酯为：4,4'-二苯基甲烷二异氰酸酯、亚苯基-1,4-二异氰酸酯、甲苯二异氰酸酯、1,4-环己基-二异氰酸酯或癸烷-1,10-二异氰酸酯中的一种。5.根据权利要求1所述的聚醚硅酮共聚物改性热塑性聚氨酯弹性体，其特征在于：扩链剂为1,4-丁二醇、乙二醇、1,2-丙二醇、2-甲基-1,3-丙二醇或1,6-己二醇。6.根据权利要求1所述的聚醚硅酮共聚物改性...
【专利技术属性】
技术研发人员：陈淑海，肖培栋，张宁，张倩，
申请(专利权)人：山东一诺威聚氨酯股份有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。