A kind of environment-friendly PVC hose material, which consists of the following parts by weight: 40 to 80 components of PVC resin; thermoplastic polyurethane elastomer 10 ~ 15; stearic acid 10 ~ 20; three two ~ 1.5 0.1 antimony oxide; iodine 4 ~ 5 and 2 ~ 4; sodium alginate; bamboo vinegar powder 0.4 ~ 0.6 from 1 to 5; carbon black; poly carbonate from 10 to 20; 2 to 4 nanometer calcium carbonate. The invention adopts adding thermoplastic polyurethane elastomer, plasticizer, heat stabilizer, antistatic agent, flame retardant PVC resin in, enhanced PVC hose low temperature resistance, flexibility, antistatic properties and flame retardant properties, the comprehensive performance of PVC composite hose preparation is good, not easy to aging, can for low temperature oil, storage and use of gas or liquid in the process.
【技术实现步骤摘要】
一种环保PVC软管材料
本专利技术涉及一种环保PVC软管材料。
技术介绍
聚氯乙烯(PVC)为微黄色半透明状,有光泽。透明度优于聚乙烯、聚苯烯,差于聚苯乙烯,随助剂用量不同,分为软、硬聚氯乙烯,软制品柔而韧、手感粘,硬制品的硬度高于低密度聚乙烯,而低于聚丙烯,在屈折处会出现白化现象。聚氯乙烯的性能比较稳定,不易被酸、碱腐蚀,对热比较耐受;具有阻燃、耐化学药品性高、机械强度和电绝缘性能高等优点。聚氯乙烯(PVC)用于制造各种软硬管材,并被广泛应用到工业、农业和广大居民生活中。随着社会经济的不断发展,对聚氯乙烯质量的要求也越来越高。现有技术中的聚氯乙烯软管,常用的PVC软管的耐低温性能差、脆性大、韧性强度低、抗老化性能差、安全性能低、运输和安装不便,制作成本高,达不到生产和生活的的要求。现有技术中提到一种卫浴洁具用纳米碳酸钙改性螺旋缠绕PVC软管的组合屋及其制备方法,但是这种材料制得的软管耐热性能较好,耐低温性能较差。
技术实现思路
针对现有技术存在的不足,本专利技术所要解决的技术问题是,提供一种耐低温、性能优良、有效提高PVC软管使用寿命的高韧性环保PVC软管材料。为解决上述技术问题,本专利技术所采取的技术方案是:一种环保PVC软管材料,由以下重量份的成分组成:聚氯乙烯树脂40~80;热塑性聚氨酯弹性体10~15;硬脂酸10~20;三氧化二锑0.1~1.5;碘酊4~5;海藻酸钠2~4;竹醋粉0.4~0.6;碳黑1~5;聚碳酸酯10~20;纳米碳酸钙2~4。本专利技术高韧性环保PVC软管材料的优点是:本专利技术采用在PVC树脂中加入热塑性聚氨酯弹性体、增塑剂、热稳 ...
【技术保护点】
一种环保PVC软管材料,其特征在于,由以下重量份的成分组成:聚氯乙烯树脂 40~80;热塑性聚氨酯弹性体 10~15;硬脂酸 10~20;三氧化二锑 0.1~1.5;碘酊 4~5;海藻酸钠 2~4;竹醋粉 0.4~0.6;碳黑 1~5;聚碳酸酯 10~20;纳米碳酸钙 2~4。
【技术特征摘要】
1.一种环保PVC软管材料,其特征在于,由以下重量份的成分组成:聚氯乙烯树脂40~80;热塑性聚氨酯弹性体10~15;硬脂酸10~...