The invention discloses a preparation method and application of a barley beta glucan polyaspartic acid compound, its preparation method is as follows: barley beta glucan, polyaspartic acid water full swelling and dissolving, adding ethylene glycol or glycerol at 80 DEG to 100 deg. the reaction time, the reaction liquid after freeze drying, the freeze-dried powder is 55 to 85 DEG C, the relative humidity is 65% ~ 85% and saturated potassium bromide or sski reaction environment for 10 ~ 20d, from highland barley dextran poly aspartic acid complexes. The compound can be used in the field of cosmetics moisturizers and bioadhesive agents. The advantage of the invention is that the compound has good moisture retention and bioadhesive properties.
【技术实现步骤摘要】
一种青稞β-葡聚糖-聚天冬氨酸复合物的制备和应用方法
本专利技术涉及生物医药
，特别涉及一种青稞β-葡聚糖-聚天冬氨酸复合物的制备和应用方法。
技术介绍
青稞β-葡聚糖是从青稞中提取得到的一类高分子非淀粉多糖，其化学结构是葡萄糖单元通过β-(1→3)和β-(1→4)苷键形成的聚合物。青稞β-葡聚糖有一定的吸水性和粘弹性，因此在化妆品保湿剂和生物粘附性药物制剂中有潜在用途。聚天冬氨酸是一种聚氨基酸，其结构是天冬氨酸单元通过肽键形成的聚合物。聚天冬氨酸有较强吸水性，常被用于合成高吸水性树脂，也被用作化妆品保湿剂。将青稞β-葡聚糖与聚天冬氨酸通过适当反应制成复合物，能改良青稞β-葡聚糖的某些性能，从而拓展其应用领域，但目前本领域尚缺乏青稞β-葡聚糖-聚天冬氨酸复合物的制备和应用方法。
技术实现思路
本专利技术针对现有技术的缺陷，提供了一种青稞β-葡聚糖-聚天冬氨酸复合物的制备和应用方法，能有效的解决上述现有技术存在的问题。为了实现以上专利技术目的，本专利技术采取的技术方案如下：一种青稞β-葡聚糖-聚天冬氨酸复合物的制备方法，包括以下步骤：步骤1、按所示重量份比例范围，...
【技术保护点】
一种青稞β‑葡聚糖‑聚天冬氨酸复合物的制备方法，其特征在于包括以下步骤：步骤1、按所示重量份比例范围，取青稞β‑葡聚糖5～9份、聚天冬氨酸0.5～3份；步骤2、加入重量份100～200的水，搅拌10～15h，使充分溶胀、溶解；步骤3、加入青稞β‑葡聚糖重量5％～15％的乙二醇，控制温度为80℃～100℃并保持恒温，搅拌4～8h，冷却；步骤4、将反应液冷冻干燥，得冻干粉；步骤5、将冻干粉置于恒温密闭容器中，控制温度为55℃～85℃并保持恒温，保持相对湿度为65％～85％，并在容器底部放置饱和溴化钾或饱和碘化钾溶液，放置10～20d。
【技术特征摘要】
1.一种青稞β-葡聚糖-聚天冬氨酸复合物的制备方法，其特征在于包括以下步骤：步骤1、按所示重量份比例范围，取青稞β-葡聚糖5～9份、聚天冬氨酸0.5～3份；步骤2、加入重量份100～200的水，搅拌10～15h，使充分溶胀、溶解；步骤3、加入青稞β-葡聚糖重量5％～15％的乙二醇，控制温度为80℃～100℃并保持恒温，搅拌4～8h，冷却；步骤4、将反应液冷冻干燥，得冻干粉；步骤5、将冻干粉置于恒温密闭容器中，控制温度为55℃～85℃并保持恒温，保持相对湿度为6...
【专利技术属性】
技术研发人员：杨文宇，李浩浩，王彬容，
申请(专利权)人：西华大学，
类型：发明
国别省市：四川,51