The invention provides an industrial furnace with slotted ladle permanent layer material and its preparation method and use method, solve the existing technology in ladle permanent layer and the working layer brick filling problems, a ladle permanent layer partition material; the ladle permanent layer partition seam material by component as follows the weight of the prepared refractory particles from 15 to 80, 5 to 20 portions of refractory powder, graphite is 1 ~ 30, 1 ~ 30 binder. The invention further provides the preparation method and application method of the permanent layer seams of the ladle. The invention provides a ladle permanent layer seating material applied to the gap between the work layer brick and the permanent layer of the ladle, which is convenient for construction, full filling and no sintering with the working layer bricks and permanent lining of the ladle, and the demolition of the work layer brick of the ladle is easy.
【技术实现步骤摘要】
一种工业窑炉用钢包永久层隔缝料及其制备方法、使用方法
本专利技术涉及工业窑炉用领域，特别是指一种工业窑炉用钢包永久层隔缝料及其制备方法、使用方法。
技术介绍
目前钢包永久层与工作层砖之间一般采用干式耐火颗粒料填充或者耐火泥浆浇灌。采用干式耐火颗粒填充在钢包工作层砖拆除时，工作层砖易分离，钢包拆除较容易，但干式耐火颗粒填充料为松散结构，填充不易密实，且容易存在空鼓现象，存在一定安全隐患。采用耐火泥浆填充的方式，耐火泥浆容易与工作层砖和永久衬烧结在一起而导致工作层砖不易拆除。
技术实现思路
本专利技术提出一种工业窑炉用钢包永久层隔缝料及其制备方法、使用方法，解决了现有技术中钢包永久层与工作层砖之间填料填充效果差的问题。本专利技术的技术方案是这样实现的：一种工业窑炉用钢包永久层隔缝料，由如下重量的成分制备而成：优选的，所述耐火颗粒的粒径为0.1～3mm，所述耐火颗粒为刚玉或莫来石或矾土或焦宝石或废钢包砖、废高铝砖、废粘土砖、废高铝浇注料的一种或几种。优选的，所述耐火粉料为粒径小于0.1mm，所述耐火粉料为刚玉或莫来石或矾土或焦宝石或废钢包砖、废高铝砖、废粘土砖、废高铝浇注料...
【技术保护点】
一种工业窑炉用钢包永久层隔缝料，其特征在于，由如下重量的成分制备而成：
【技术特征摘要】
1.一种工业窑炉用钢包永久层隔缝料，其特征在于，由如下重量的成分制备而成：2.如权利要求1所述的一种工业窑炉用钢包永久层隔缝料，其特征在于：所述耐火颗粒的粒径为0.1～3mm，所述耐火颗粒为刚玉或莫来石或矾土或焦宝石或废钢包砖、废高铝砖、废粘土砖、废高铝浇注料的一种或几种。3.如权利要求1所述的一种工业窑炉用钢包永久层隔缝料，其特征在于：所述耐火粉料为粒径小于0.1mm，所述耐火粉料为刚玉或莫来石或矾土或焦宝石或废钢包砖、废高铝砖、废粘土砖、废高铝浇注料的一种或几种。4.如权利要求1所述的一种工业窑炉用钢包永久层隔缝料...
【专利技术属性】
技术研发人员：曹仁锋，张晓波，杨少康，张晗，刘丽，车晓梅，刘美荣，王伟伟，赵冉，于九利，胡玲军，刘洋，张盛，
申请(专利权)人：北京利尔高温材料股份有限公司，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。