一种以γ‑Al2O3为载体的脱硝催化剂及其制备方法技术

本发明专利技术公开了一种以γ‑Al2O3为载体的脱硝催化剂及其制备方法，该脱硝催化剂包括γ‑Al2O3、WO3、纳米BaSO4及杂多酸；制法包括：将WO3、纳米BaSO4及杂多酸混匀后，加入γ‑Al2O3载体，浸渍，制得脱硝催化剂浆料，经干燥，焙烧后，即可。优点为该脱硝催化剂具有较低的起活温度、脱硝效率高；同时，该制法简单，可操作性强，降低了生产成本。

A denitration catalyst carrier and preparation method thereof to gamma Al2O3

The invention discloses a denitration catalyst carrier and preparation method thereof to gamma Al2O3, the denitration catalyst including Al2O3, WO3, gamma nano BaSO4 and heteropoly acid; the preparation method comprises: WO3, nano BaSO4 and heteropoly acid after mixing, adding gamma Al2O3 carrier, impregnated, prepared denitration the catalyst slurry, drying, roasting, can. The advantage is that the denitrification catalyst has low living temperature and high denitrification efficiency. At the same time, this method is simple, easy to operate, and reduces the production cost.

【技术实现步骤摘要】
一种以γ-Al2O3为载体的脱硝催化剂及其制备方法
本专利技术属于催化剂领域，尤其涉及一种以γ-Al2O3为载体的脱硝催化剂及其制备方法。
技术介绍
现有的SCR脱硝催化剂中，以V2O5为活性组分，TiO2为载体的钒钛系脱硝催化剂工业应用程度最高。现已有众多的钒钛系脱硝催化剂的制备方法及脱硝工艺在本领域公开，如记载在申请号或者专利号为CN101829560B、CN103240078B、CN101791518B、CN102989484等专利技术中。而在我国燃煤电厂的实际工况中，由于烟气成分复杂、温度变化大、对脱硝催化剂的活性、热稳定性以及寿命都有着较高的要求，同时，又由于传统的锐钛矿型TiO2载体存在比表面积较小、传质效率较低以及在高温的烟气环境中容易烧结，转化成为金红石相等缺点。
技术实现思路
本专利技术的第一目的是提供一种脱硝效率高且水热稳定性强的以γ-Al2O3为载体的脱硝催化剂；本专利技术的第二目的是提供该脱硝催化剂的制备方法。技术方案：本专利技术以γ-Al2O3为载体的脱硝催化剂，按重量份计包括如下原料：γ-Al2O370-150份、WO360-100份、纳米BaSO410-30本文档来自技高网...

【技术保护点】
一种以γ‑Al2O3为载体的脱硝催化剂，其特征在于按重量份计包括如下原料：γ‑Al2O3 70‑150份、WO3 60‑100份、纳米BaSO4 10‑30份及杂多酸10‑30份。

【技术特征摘要】
1.一种以γ-Al2O3为载体的脱硝催化剂，其特征在于按重量份计包括如下原料：γ-Al2O370-150份、WO360-100份、纳米BaSO410-30份及杂多酸10-30份。2.根据权利要求1所述的以γ-Al2O3为载体的脱硝催化剂，其特征在于：所述杂多酸包括12-钨磷酸、12-钨硅酸或12-钼硅酸。3.根据权利要求1所述的以γ-Al2O3为载体的脱硝催化剂，其特征在于：所述γ-Al2O3的重量份数为100-130份。...

【专利技术属性】
技术研发人员：周丽，
申请(专利权)人：周丽，
类型：发明
国别省市：江苏,32