一种用于丙烷完全燃烧的催化剂及其制备方法技术
A catalyst for complete combustion of propane and its preparation method
A catalyst for propane complete combustion and a preparation method thereof, catalyst carrier and active component, Fe3O4 LaF3 CeF3 carrier BN, Fe3O4, LaF3, CeF3 mass percentage, BN 0.05: (0.5 1.5 (0.5): 1.5 (0.1): 0.3); group activity is Rh and Pd, Rh and Pd content as the carrier of 2wt%, Rh, Pd in which the quality ratio is (1 ~ 4): 1. The catalyst prepared by CO impregnation method to prepare Fe3O4 LaF3 CeF3 BN vector, then Rh, Pd Fe3O4 LaF3 CeF3 to load vector BN by impregnation, after frying, drying and roasting to obtain. The catalyst can completely oxidize the propane at low temperature, and the catalyst has the advantages of simple process, high activity and good stability.
【技术实现步骤摘要】
一种用于丙烷完全燃烧的催化剂及其制备方法
本专利技术涉及一种化学催化剂及其制备方法，尤其涉及一种用于丙烷完全燃烧的催化剂及其制备方法
技术介绍
随着工业的快速发展，环境污染问题，尤其是空气污染已经成为当今人们最关注的的问题之一。大气中的挥发性有机物与NOX光照情况下发生光化学反应，导致光化学反应，产生臭氧及其光化学烟雾污染。因此，减少大气中挥发性有机物的污染是改善大气环境的关键。在挥发性有机物中，烷烃是最难氧化的一类有机物，催化剂燃烧是消除这些有机物的有效手段。如何开发研制更为高效的烷烃类挥发性有机物的消除催化剂是一直努力的目标。丙烷是烷烃中比较有代表性的物质，中国专利CN103990460A和中国专利CN103990461A公开了一种将不同过渡金属盐溶液滴入碱性溶液中，经过洗涤、干燥、焙烧得到一系列对丙烷催化氧化的不同过渡金属氧化物催化剂。该系列催化剂对丙烷进行催化氧化，达到90％丙烷转化率的最低温度基本超过250℃，且由于催化剂在300℃空气气氛中焙烧3小时制得，导致催化剂的应用范围受到限制。除此之外，由于该方法要将过渡金属加入到碱溶液中，洗涤产生的废液过多，...
【技术保护点】
一种用于丙烷完全燃烧的催化剂，其特征在于：该催化剂由载体和活性组分组成，载体为Fe3O4‑LaF3‑CeF3‑BN，其中Fe3O4、LaF3、CeF3、BN的质量百分比为0.05:(0.5‑1.5):(0.5‑1.5):(0.1‑0.3)；活性组分是Rh和Pd，Rh和Pd总质量百分含量为载体的2wt％，其中Rh、Pd的质量比是(1～4):1。
【技术特征摘要】
1.一种用于丙烷完全燃烧的催化剂，其特征在于：该催化剂由载体和活性组分组成，载体为Fe3O4-LaF3-CeF3-BN，其中Fe3O4、LaF3、CeF3、BN的质量百分比为0.05:(0.5-1.5):(0.5-1.5):(0.1-0.3)；活性组分是Rh和Pd，Rh和Pd总质量百分含量为载体的2wt％，其中Rh、Pd的质量比是(1～4):1。2.权利要求1所述催化剂的制备方法，其特征在于：采用共浸渍法，具体步骤如下：(1)Fe3O4-LaF3-CeF3-BN载体...
【专利技术属性】
技术研发人员：罗孟飞，刘艳荣，李雪，宋建冬，
申请(专利权)人：浙江师范大学，
类型：发明
国别省市：浙江,33