一种用于软骨损伤修复的细胞‑支架复合材料制备方法及应用技术
A method and application of cell scaffold composite material preparation for repairing cartilage injury
The present invention provides a method for repairing cartilage defect cell scaffold composite material preparation method and application thereof, belonging to the field of bone tissue engineering and regenerative medicine. The seed cells of the scaffold composite material prepared with multipotential differentiation, better safety of reprogrammed cells, scaffolds using konjac glucomannan and sodium hyaluronate mixed preparation of biological materials, cell and scaffold by co culture method to obtain cell scaffold composite material. The composite material preparation method is simple, cell scaffold composite material preparation can effectively repair cartilage damage in bone tissue engineering and regenerative medicine, especially has broad application prospects in the field of cartilage repair.
【技术实现步骤摘要】
一种用于软骨损伤修复的细胞-支架复合材料制备方法及应用
本专利技术涉及一种用于软骨损伤修复的细胞-支架复合材料制备方法及应用，属于骨组织工程和再生医学领域。
技术介绍
软骨组织是一种蛋白多糖、胶原和透明质酸等物质含量丰富的组织，但血液供应和软骨细胞数量缺乏，因此，软骨组织一旦受损，即便是微小的软骨损伤也难以自然修复或愈合。目前，临床上常用的关节软骨损伤修复方法主要有软骨和软骨下骨去除、微骨折和软骨下骨钻孔、自体骨软骨移植和同种异体骨软骨移植、软骨或骨膜移植等（刘效仿，等.中华创伤骨科杂志，2014,16(6):537-539）。在这些方法中，由于自体骨软骨移植方法具有安全、有效等优点，是临床最为常用的治疗方法，但是该方法最大的弊端在于，自体骨软骨采集不但会给患者带来新的创伤，同时也给患者带来严重的心理和生理负担。而异体骨软骨移植虽然可成为临床上治疗软骨损伤的替代材料，但由于供体限制，难以大幅应用，同时还可能存在严重的免疫排斥反应和疾病传播风险。微骨折和软骨下骨钻孔也是较为常用的软骨修复方法，能够通过微骨折和软骨下骨钻孔使干细胞到达缺损部位，但由于局部环境和机械应力...
【技术保护点】
一种用于软骨损伤修复的细胞‑支架复合材料制备方法，其特征在于，复合材料中所使用的细胞为鱼卵母细胞提取物诱导成纤维细胞产生的重编程细胞，复合材料中所使用的支架为魔芋葡甘聚糖（KGM）和透明质酸钠（HA）通过冷冻干燥法制备的复合支架KGM/HA。
【技术特征摘要】
1.一种用于软骨损伤修复的细胞-支架复合材料制备方法，其特征在于，复合材料中所使用的细胞为鱼卵母细胞提取物诱导成纤维细胞产生的重编程细胞，复合材料中所使用的支架为魔芋葡甘聚糖（KGM）和透明质酸钠（HA）通过冷冻干燥法制备的复合支架KGM/HA。2.一种用于软骨损伤修复的细胞-支架复合材料制备方法，其特征在于，重编程细胞与KGM/HA支架复合材料制备方法为：用含有10%胎牛血清的DMEM/F12培养基制备1×106个/ml的重编程细胞悬液，并接种于六孔板中的无菌复合材料KGM/HA上，每孔加入重编程细胞悬液5ml，加入完成后，将六孔板置于37℃、5%CO2、...
【专利技术属性】
技术研发人员：潘兴华，朱向情，陈强，陈庆华，
申请(专利权)人：陈强，
类型：发明
国别省市：云南,53