一种铜银钎焊母料及其钎焊工艺制造技术

本发明专利技术提供了一种铜银钎焊母料及其钎焊工艺，涉及汽车工业领域。本发明专利技术提供一种铜银钎焊母料，通过银元素和铜元素形成共晶，钎料向母材扩散充分；浸润性良好，可应用于精密的焊接，且银和铜都具有良好的热传递性能，可以广泛应用于需要传热、换热工件的焊接；钎焊工艺操作简单，焊件结构较好，性能较优，焊接工件结构稳定，硬度和强度都较好，焊缝组织呈均匀一体化。

A copper silver brazing master batch and its brazing process

The invention provides a copper silver brazing master batch and its soldering process, which relates to the field of automobile industry. The present invention provides a copper silver brazing masterbatch, forming eutectic by elemental silver and copper, solder to the parent material diffusion sufficiently; good wettability, can be used in precision welding, and silver and copper has good heat transfer performance, welding can be widely applied to the heat transfer, heat transfer member; brazing process simple operation, good welding structure, excellent performance, stable welding structure, hardness and strength are better weld microstructure was uniform and integration.

【技术实现步骤摘要】
一种铜银钎焊母料及其钎焊工艺
本专利技术涉及汽车工业领域，且特别涉及一种铜银钎焊母料及其钎焊工艺。
技术介绍
散热器作为汽车的核心部件，其性能质量显得尤为重要。提高散热器的散热能力是各个汽车生产厂家急需解决的问题。由于铝材本身固有的局限性，以及铜更好散热性、更高的热导率、更大的自由通流截面积和更低的气流速度和风阻，目前散热器材料朝着偏向于以铜及其合金作为散热器主材方向发展，新的材料带来必然带来了新的连接技术，而铜硬钎焊技术具有较好设计特性，因而得到了广泛的应用。在汽车实际生产中，欧美和日本开始广泛采用此类技术并取得了巨大的成功。散热器质量与焊缝性能关系密切，因此研究铜的焊缝性能显得极其有意义，铜的硬钎焊过程中，必然存在着母材和钎料之间相互扩散，即熔化后的钎料向母材中扩散，母材向钎料中扩散。另外由于受到母材成分、钎料成分、加热温度、保温时间、焊缝间隙、表面清洁度等一系列加工工艺的影响，焊缝组织会表现出多元化，并非我们所熟知的单一固溶体、化合物、共晶体形态，而表现出多种形态，可能是上述形态相互结合的产物，这样势必会对焊接接头的性能造成影响。
技术实现思路
本专利技术的目的在于提供一种铜银钎焊本文档来自技高网...

【技术保护点】
一种铜银钎焊母料，其特征在于，所述铜银钎焊母料包括铜27‑29wt％；银71‑73wt％。

【技术特征摘要】
1.一种铜银钎焊母料，其特征在于，所述铜银钎焊母料包括铜27-29wt％；银71-73wt％。2.根据权利要求1所述的铜银钎焊母料，其特征在于，所述铜银钎焊母料包括铜27.5-28.5wt％；银71.5-72.5wt％。3.根据权利要求1所述的铜银钎焊母料，其特征在于，所述铜银钎焊母料的钎焊温度为800-1000℃。4.如权利要求1-3任一项所述的铜银钎焊母料在钎焊中应用。5.一种使用铜银钎焊母料的钎焊工艺，其特征在于，对去膜的工件使用铜银钎焊母料进行真空钎焊。6.根据权利要求5所述的使用铜银钎焊母料的钎焊工艺，其特征在于，包括以下步骤：所述去膜包括对工件进行磨...

【专利技术属性】
技术研发人员：李聪，曹小琳，
申请(专利权)人：湖北汽车工业学院，
类型：发明
国别省市：湖北,42