The invention belongs to the technical field of rubber track. The invention discloses a brass plated steel cord rubber track, which is composed of rubber and embedded in the internal rubber brass plated steel cord, rubber by Zinc Oxide, natural rubber, stearic acid, pine tar, anti-aging agent, accelerator, carbon black, white carbon black, sulfur and other raw materials for adhesives well. The invention of the brass plated steel cord rubber crawler has excellent heat resistance and high temperature properties, can be used continuously in a high temperature environment; has excellent anti-aging properties, with a longer life, but also to reduce the track replacement frequency in the use process; strong wear resistance, the use of longer life, the replacement cycle longer.
【技术实现步骤摘要】
一种镀黄铜钢丝帘线橡胶履带
本专利技术涉及橡胶履带
，尤其是涉及一种镀黄铜钢丝帘线橡胶履带。
技术介绍
橡胶履带主要是针对特殊场合而使用，像阅兵式的时候，坦克，装甲车等，保护地面！橡胶履带行走系统，噪声低，振动小，乘坐舒适，特别适合于高速转移多的场合，实现了全路面通过性能。先进可靠的电器仪表及整机状态监控系统，为驾驶员正确操纵提供了可靠的保证。除了应用于军事外，也广泛用于大型机械，如挖土机等履带车辆，其功能性和作用相同。但是相比于钢制或其他材质的履带，其耐用性一直是一个较大的短板，一来是橡胶自身存在的易老化的特点，其老化后性能下降严重，造成橡胶履带使用寿命短，更换周期短等缺点，二来是橡胶还存在耐磨性能差，在重负载的情况下其不耐磨的特点使得磨损严重，也造成了其寿命较短的缺点；因此在对橡胶履带的结构进行改进的同时，还需要对橡胶履带所采用的橡胶进行适应性的改性，增强其耐磨性能和抗老化性能。
技术实现思路
为解决上述问题，本专利技术提供了一种具有优异耐热耐高温特性并且具有优良耐老化性能的镀黄铜钢丝帘线橡胶履带。为实现上述目的，本专利技术采用的技术方案如下：一种镀黄铜钢丝...
【技术保护点】
一种镀黄铜钢丝帘线橡胶履带，其由橡胶胶料和嵌在橡胶胶料内部的镀黄铜钢丝帘线组成，其特征在于所述的橡胶胶料包含以下重量份的原料：天然橡胶100份，氧化锌8～12份，硬脂酸2.8～3.2份，松焦油5.8～6.2份，防老剂1.9～2.1份，促进剂1.1～1.5份，炭黑40～50份，白炭黑23～27份，硫黄2.8～3.2份，粘合剂2.7～3.3份。
【技术特征摘要】
1.一种镀黄铜钢丝帘线橡胶履带，其由橡胶胶料和嵌在橡胶胶料内部的镀黄铜钢丝帘线组成，其特征在于所述的橡胶胶料包含以下重量份的原料：天然橡胶100份，氧化锌8～12份，硬脂酸2.8～3.2份，松焦油5.8～6.2份，防老剂1.9～2.1份，促进剂1.1～1.5份，炭黑40～50份，白炭黑23～27份，硫黄2.8～3.2份，粘合剂2.7～3.3份。2.根据权利要求1所述的一种镀黄铜钢丝帘线橡胶履带，其特征在于所述的橡胶胶料包含以下重量份的原料：天然橡胶100份，氧化锌10份，硬脂酸3份，松焦...
【专利技术属性】
技术研发人员：闻浩泉，赵立案，倪志文，沈爱仙，杨建，穆祥松，
申请(专利权)人：浙江久运汽车零部件有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。