一种移动终端后壳制造方法、移动终端后壳及移动终端技术
Method for manufacturing rear shell of mobile terminal, mobile terminal, rear shell and mobile terminal
The invention discloses a mobile terminal shell manufacturing method, mobile terminal and mobile terminal shell, relates to a mobile terminal shell technology, manufacturing process to solve the existing mobile terminal shell complex technical problems, high cost of manufacturing process. Including the mobile terminal after the shell manufacturing method: providing a mobile terminal after the shell mold; the light metal alloy melt filling to the mobile terminal after the shell mold casting, forming a preform mobile terminal shell; on the preformed mobile terminal shell of closed die forging, the formation of mobile terminal shell. The invention relates to a manufacturing method of a mobile terminal rear shell, which is applied to manufacturing a mobile terminal shell.
【技术实现步骤摘要】
本专利技术涉及移动终端壳体
，尤其涉及一种移动终端后壳制造方法、移动终端后壳及移动终端。
技术介绍
目前，移动终端制造业大多采用CNC机床(Computernumericalcontrol计算机数字控制)生产制造移动终端后壳。然而，采用CNC机床制造移动终端后壳时，需要对预成型移动终端后壳进行多次多级数控加工，在每次每级数控加工时均需要对预成型移动终端后壳重新进行夹持定位，从而使得移动终端后壳的整个制造过程工序繁琐、工艺路线冗长、成品加工工时较长，进而导致移动终端后壳的制造工艺成本较高。
技术实现思路
本专利技术的目的在于提供一种移动终端后壳制造方法、移动终端后壳及移动终端，用于简化移动终端后壳的制造工序，降低移动终端后壳的制造工艺成本。为达到上述目的，本专利技术提供一种移动终端后壳制造方法，采用如下技术方案：该移动终端后壳制造方法包括：提供一移动终端后壳模具；将轻金属合金熔体充型到所述移动终端后壳模具中，压铸形成预成型移动终端后壳；对所述预成型移动终端后壳进行闭模锻造，形成移动终端后壳。与现有技术相比，本专利技术提供的移动终端后壳制造方法具有以下有益效果：在...
【技术保护点】
一种移动终端后壳制造方法，其特征在于，包括：提供一移动终端后壳模具；将轻金属合金熔体充型到所述移动终端后壳模具中，压铸形成预成型移动终端后壳；对所述预成型移动终端后壳进行闭模锻造，形成移动终端后壳。
【技术特征摘要】
1.一种移动终端后壳制造方法，其特征在于，包括：提供一移动终端后壳模具；将轻金属合金熔体充型到所述移动终端后壳模具中，压铸形成预成型移动终端后壳；对所述预成型移动终端后壳进行闭模锻造，形成移动终端后壳。2.根据权利要求1所述的移动终端后壳制造方法，其特征在于，将轻金属合金熔体充型到所述移动终端后壳模具中，压铸形成预成型移动终端后壳的具体步骤为：将轻金属合金熔体低速充型到所述移动终端后壳模具中，压铸形成预成型移动终端后壳。3.根据权利要求1所述的移动终端后壳制造方法，其特征在于，所述移动终端后壳制造方法还包括：对所述移动终端后壳进行整形处理。4.根据权利要求3所述...