The present invention relates to an abrasive material, consisting of white corundum powder and silicon carbide powder, its preparation method is as follows: (1) the white corundum and boron carbide in kerosene soaked for 48 to 56 hours; when soaking, soaking kerosene is higher than that of material 3~5 cm; (2) quantity, take after soaking Bai Gang jade and silicon carbide, which accounted for 2/3 SiC quality copies, accounting for 1/3 white corundum quality copies; (3) the grinding tool with vise clamping workpiece, grinding, grinding, grinding apparatus used for reinforcing bar pressure grinding, and hand sensing grinding effect in the grinding process, inspection notice. The abrasive material of the invention adopts the mode of mixing the white corundum micropowder and the silicon carbide powder to improve the use effect, and is easy to avoid the lack of use, and is convenient to use according to the need.
【技术实现步骤摘要】
本专利技术涉及一种研磨料及其制备方法，属于机械加工
技术介绍
机械工件加工要求有比较高的精度，所以工件在加工完成后都需要对加工后的工件进行研磨，使其能够达到一定的精度要求。现在普遍的加工研磨材料都是氧化铁液态研磨料进行研磨，虽然也能完成研磨任务，但是在使用过程中这种研磨料中的氧化铁和硝酸如果在液态研磨料中的占比太小，则研磨切削效果不理想，为此必须要加大占比才能使得效果有好转。在研磨机上的磨盘告诉旋转时，与加工面磨擦产生热量，使氧化铁粉末到处飞溅，这种方式存在安全隐患又不环保。
技术实现思路
本专利技术的目的在于提供一种研磨料及其制备方法，以便生产制备出更加合理，使用效果好的研磨料。为了实现上述目的，本专利技术的技术方案如下。一种研磨料，由白刚玉微粉和碳化硅粉末组成，其制备方法如下：（1）将白刚玉和碳化硼在煤油中浸泡48～56小时；浸泡时，煤油的浸泡高于物料3~5厘米；（2）配量，取浸泡后的白刚玉和碳化硅，其中，碳化硅质量份数占2/3，白刚玉质量份数占1/3；（3）将研磨工具用虎台钳夹紧工件，进行研磨，研磨时，针对研磨器具采用加力杆加压研磨，并用手感知研磨效...
【技术保护点】
一种研磨料，其特征在于：由白刚玉微粉和碳化硅粉末组成，其制备方法如下：（1）将白刚玉和碳化硼在煤油中浸泡48～56小时；浸泡时，煤油的浸泡高于物料3~5厘米；（2）配量，取浸泡后的白刚玉和碳化硅，其中，碳化硅质量份数占2/3，白刚玉质量份数占1/3；（3）将研磨工具用虎台钳夹紧工件，进行研磨，研磨时，针对研磨器具采用加力杆加压研磨，并用手感知研磨效果，研磨过程中注意检验。
【技术特征摘要】
1.一种研磨料，其特征在于：由白刚玉微粉和碳化硅粉末组成，其制备方法如下：（1）将白刚玉和碳化硼在煤油中浸泡48～56小时；浸泡时，煤油的浸泡高于物料3~5厘米；（2）配量，取浸泡后的白刚玉和碳化硅，其中，碳化硅质量份数占2/3，白刚玉质量份数占1/3；（3）将研磨工具用虎台钳夹紧工件，进行研磨，研磨时，针对研磨器具采用加力杆加压研磨，并用手感知研磨效果，研磨过程中注意检验。2.根据权利要求1所述的研磨料，其特征在于：白刚玉、碳化硅浸泡前需要予以清洁处理，保持表面清洁状态。3.根据权利要求1所述的...
【专利技术属性】
技术研发人员：张从鑫，黄景高，张应刚，
申请(专利权)人：中山市捷上同程数控机床有限公司，
类型：发明
国别省市：广东;44