Carburizing protection method
The invention relates to a carburizing protection method, the method comprises the following steps: 1), the processed parts fixed on a rotating table, both ends of the A and B induction heating coil installed in quenching transformer; 2), internal cooling water is injected into the high pressure sensor, induction heating coil into intermediate frequency current, workpiece rotation, induction heating coil fork root to slowly move; 3), machined parts in induced current, through the principle of electromagnetic induction heating, in the processing of parts of the fork of the formation of local vortex, make the processed parts fork is heated by the invention; induction heating parts tempering process, high production efficiency, less material consumption, and surface hardness after tempering consistency and subsequent machining process is stable.
【技术实现步骤摘要】
本专利技术属于防护方法
，尤其涉及一种渗碳防护方法。
技术介绍
被加工零件采用表面渗碳处理，整个表面硬度达到HRC59-62，深度0.8-1.2mm，感应线圈包围部位为叉部，还需加工万向节安装孔和卡簧槽，表面硬度太高加工不了。如果使用传统的工艺方法是在渗碳前叉部表面用防渗剂包裹，渗碳后再去除，存在去除困难等问题，工作效率太低。采用防渗剂降低叉部表面硬度，需要在渗碳前进行防渗剂涂覆，完成淬火后去除防渗剂，不仅存在生产效率低，而且需要消耗防渗剂材料，且存在渗碳过程中防渗剂脱落造成局部硬度偏高，使后续加工尺寸不稳定等问题。脱落的防渗涂料又会污染渗碳淬火油，影响淬火油的冷却效果。
技术实现思路
本专利技术的目的在于克服现有技术存在的不足，而提供一种渗碳防护方法，采用感应加热进行零件局部回火工艺，不仅生产效率高，材料消耗少，而且回火后零件表面硬度一致性好，后续机加工过程稳定。本专利技术的目的是通过如下技术方案来完成的，该方法包括如下步骤：1)、被加工零件固定在一个可旋转的工作台上，感应加热线圈的A、B两端安装在淬火变压器上；2)、感应器内部通入高压的冷却水，感应加热线圈...
【技术保护点】
一种渗碳防护方法，其特征在于：该方法包括如下步骤：1)、被加工零件(1)固定在一个可旋转的工作台上，感应加热线圈(2)的A、B两端安装在淬火变压器上；2)、感应器内部通入高压的冷却水，感应加热线圈(2)通入中频电流后，被加工零件(1)旋转，感应加热线圈(2)自叉部的根部向上慢慢移动；3)、被加工零件(1)在感应电流的作用下，通过电磁感应加热原理，在被加工零件(1)的叉部形成局部的涡流，使被加工零件(1)叉部被加热。
【技术特征摘要】
1.一种渗碳防护方法，其特征在于：该方法包括如下步骤：1)、被加工零件(1)固定在一个可旋转的工作台上，感应加热线圈(2)的A、B两端安装在淬火变压器上；2)、感应器内部通入高压的冷却水，感应加热线圈(2)通入...