一种熔铝设备内衬砌筑结构，内衬熔池用高铝砖与不定形耐火材料浇注料混合砌筑。每五块高铝砖采用全丁式搭接错缝砌筑，呈工字形；相邻的每五块高铝砖之间留空为十字形，填充为不定形耐火材料浇注料。同层相邻错开的两块高铝砖之间间距为112mm至116mm之间。本实用新型专利技术的内衬砌筑结构可以使高铝砖与浇注料充分结合，二者的接触面积大大增加，提高了炉体内衬的保温性能，可使其在高温作用下能够高效运作。其主要效果在于能够提高炉衬保温性能，延长炉子的使用寿命。

Lining structure of molten aluminium equipment

The utility model relates to a lining structure for an aluminium melting equipment, which is lined with high alumina bricks and is mixed with unshaped refractory castables. Each of the five pieces of high aluminum brick by Ding overlapping staggered masonry is I-shaped; space between every five adjacent blocks of high aluminum brick is crisscross, filled with amorphous refractory castable. The distance between the two blocks of high alumina bricks staggered from the same floor is between 112mm and 116mm. Lining structure of the utility model can make the high aluminum brick castable and fully integrated, the contact area of the two increase greatly, improve the furnace lining insulation performance, enabling it to operate efficiently at high temperature. The main effect is that it can improve the heat preservation performance of the lining and prolong the service life of the furnace.

【技术实现步骤摘要】
一种熔铝设备内衬砌筑结构
本技术涉及铝加工行业冶炼设备，特别指一种熔铝设备内衬砌筑结构。
技术介绍
随着耐火材料技术的发展，不定型耐火材料在性能、施工及寿命等各方面的优越性越来越明显，大有取代定型耐火材料的趋势。但随之带来了施工方法的问题，如何解决采用不定型耐火材料的大型及超大型炉子内衬耐火材料易开裂、损坏、瘫塌的问题，则成为当务之急。
技术实现思路
本技术要解决的技术问题是炉衬热态线性变化及高温熔融状态下引起的炉衬瘫塌、开裂，为解决上述问题，提供一种熔铝设备内衬砌筑结构。本技术的目的是以下述方式实现的：一种熔铝设备内衬砌筑结构，内衬熔池用高铝砖与不定形耐火材料浇注料混合砌筑。每五块高铝砖采用全丁式搭接错缝砌筑，呈工字形；相邻的每五块高铝砖之间留空为十字形，填充为不定形耐火材料浇注料。其中，同层相邻错开的两块高铝砖之间间距为112mm至116mm。炉衬耐火材料设计应充分考虑高温设备熔炼工艺的特点，考虑熔池、侧墙、炉顶工况及载荷变化的不同，分别作针对性结构设计。本技术的内衬砌筑结构可用于熔铝炉，保温炉等炉体，采用优质不定型耐火材料分块施工及锚固施工技术，高铝砖与浇注料相结合的复合施工方式，其中本文档来自技高网...

【技术保护点】
一种熔铝设备内衬砌筑结构，其特征在于：内衬熔池用高铝砖与不定形耐火材料浇注料混合砌筑。

【技术特征摘要】
1.一种熔铝设备内衬砌筑结构，其特征在于：内衬熔池用高铝砖与不定形耐火材料浇注料混合砌筑。2.根据权利要求1所述的熔铝设备内衬砌筑结构，其特征在于：每五块高铝砖采用全丁式搭接错缝砌筑，呈工...