一种大型半自磨机衬板制造技术
Lining plate of large semi autogenous grinding machine
The utility model relates to the improvement of a large semi autogenous mill, in particular to an improved lining plate of a large semi autogenous grinder. A large semi self mill liner, the liner is installed in the semi self mill barrel through three bolts, the overall height is 190mm, the thickness of the base plate will be reduced from 90mm to 75 80mm, unchanged overall height, installation of multi block rib on the second to the third bolt bolt direction, the rib thickness is 50mm and the gap between the two rib plate is 50mm and the height of stiffened plate is 250 280mm. The utility model has the advantages that the service life of the lining plate is prolonged, the operation rate of the mill is improved, and the production is continuously and stably operated.
【技术实现步骤摘要】
一种大型半自磨机衬板
本技术涉及一种大型半自磨机的改进，具体是一种大型半自磨机衬板改进。
技术介绍
太钢集团岚县矿业公司的设计能力为年产铁精矿粉741万t，属于大型选矿厂，有三台￠10.37M×5.49M半自磨机，主要通过钢球和原矿相互自磨后，通过水把矿浆排出磨机，所以磨机衬板的寿命成为磨机作业率的关键因素。一系列于2012年8月份运行，二、三系列于12月份运行，目前，半自磨机筒体衬板使用寿命只有55天左右，造成检修次数频繁，且检修时间较长，无法保证设备作业率，增加运行成本，严重影响全年生产任务的顺利完成。因此寻求、开发长寿命半自磨衬板迫在眉睫。
技术实现思路
本技术所要解决的技术问题是：如何提高半自磨机筒体衬板使用寿命。本技术所采用的技术方案是：一种大型半自磨机衬板，该衬板通过三条螺栓安装在半自磨机筒体里，整体高度为190mm，将底板厚度由90mm减为75-80mm，整体高度不变，在第二螺栓朝向第三螺栓的方向安装多块筋板，筋板厚度为50mm，两筋板之间的间隙为50mm，筋板高度为250-280mm。作为一种优选方式：该半自磨机衬板通过铸造一体化成型。本技术的有益效果是：延长了衬板使用寿命，提高磨机作业率，保证生产连续稳定运行。附图说明图1是本技术的结构示意图；图2是本技术筋板结构示意图；其中，1、圆弧槽，2、第一螺丝孔，3、第二螺丝孔，4、第三螺栓孔，5、筋板。具体实施方式如图1和图2所示，本技术装置是在现有大型半自磨机衬板基础上的改进，具体改进点如下1、衬板底板不磨损，将该部位厚度减薄，将衬板底板厚度由90mm减为75-80mm；衬板底板是指圆弧槽底部到衬...
【技术保护点】
一种大型半自磨机衬板，该衬板通过三条螺栓安装在半自磨机筒体里，整体高度为190mm，其特征在于：将底板厚度由90mm减为75‑80mm，整体高度不变，在第二螺栓朝向第三螺栓的方向安装多块筋板，筋板厚度为50mm，两筋板之间的间隙为50mm，筋板高度为250‑280mm。
【技术特征摘要】
1.一种大型半自磨机衬板，该衬板通过三条螺栓安装在半自磨机筒体里，整体高度为190mm，其特征在于：将底板厚度由90mm减为75-80mm，整体高度不变，在第二螺栓朝向第三螺栓的方向...