The invention discloses a flue gas denitration catalyst and a preparation method thereof. The flue gas denitration catalyst comprises a carrier and an active substance, wherein the carrier is composed of LaMnO3 and TiO2, and the active substance is composed of V2O5 and Pd. The mass ratio of LaMnO3 to TiO2 is 1:6 ~ 6. Based on the carrier mass, the content of V2O5 is 0.5 ~ 10%, and the content of Pd is 0.01 ~ 0.15%. The invention has the beneficial effect. The catalyst of the invention has the advantages of simple preparation method, the removal of the prepared denitration catalyst for high concentration of nitrogen oxides, especially nitrogen oxide removal at low temperature under 200 DEG C, the denitrification efficiency of more than 80%, suitable for all kinds of steel pickling line of flue gas denitrification.
【技术实现步骤摘要】
烟气脱硝催化剂及其制备方法
本专利技术属于催化剂合成制备
，特别是涉及钢铁酸洗烟气脱硝催化剂，以及该催化剂的制备方法。
技术介绍
铁厂在不锈钢表面处理过程中，广泛采用HF+HNO3混酸酸洗，因此产生高浓度的NOx废气，由于NO2的含量较高，表现为烟囱“冒黄龙”现象，必须采取切实可行的方法予以处理。其中NH3-SCR技术较为成熟可靠。酸洗NOx废气具有低温、微尘、不含SO2及CO等、浓度高或者浓度波动大、氧化度高等特点。随着国家对火电、冶炼、钢铁等行业NOX排放的严格要求，适用于钢铁酸洗烟气低温、氮氧化物浓度高等特点脱硝催化剂迫在眉睫。
技术实现思路
本专利技术的第一目的是提供一种烟气脱硝催化剂，本专利技术的第二目的是提供一种烟气脱硝催化剂的制备方法，以解决现有催化剂脱硝效率低的问题。为了实现上述第一目的，本专利技术提供一种烟气脱硝催化剂，包括载体和活性物质，所述载体由LaMnO3和TiO2构成；所述活性物质由V2O5和Pd构成。本专利技术如上所述的烟气脱硝催化剂，优选的，LaMnO3与TiO2的质量比为1:6～6；以载体质量为基准，V2O5的含量为0.5～10%...
【技术保护点】
一种烟气脱硝催化剂，包括载体和活性物质，其特征在于：所述载体由LaMnO3和TiO2构成；所述活性物质由V2O5和Pd构成。
【技术特征摘要】
1.一种烟气脱硝催化剂，包括载体和活性物质，其特征在于：所述载体由LaMnO3和TiO2构成；所述活性物质由V2O5和Pd构成。2.根据权利要求1所述的烟气脱硝催化剂，其特征在于，LaMnO3与TiO2的质量比为1:6～6；以载体质量为基准，V2O5的含量为0.5～10%，Pd的含量为0.01～0.15%。3.根据权利要求1所述的烟气脱硝催化剂，其特征在于，LaMnO3与TiO2的质量比为1:5～5；以载体质量为基准，V2O5的含量为1.5～5%，Pd的含量为0.01～0.1%。4.根据权利要求1-3任一项所述的烟气脱硝催化剂，其特征在于，所述V2O5的前驱体是偏钒酸铵、硫酸氧钒、乙酰丙酮氧钒中的一种或多种。5.根据权利要求4所述的烟气脱硝催化剂，其特征在于，所述Pd的前驱体可以是氯化钯、醋酸钯、二氯四氨钯中的一种或多种。6.权利要求5所述的烟气脱硝催化剂的制备方法，包括以下步骤：步骤1，利用燃烧法制备LaMnO3；步...
【专利技术属性】
技术研发人员：肖雨亭，陆金丰，周凤翔，徐光辉，
申请(专利权)人：北京国电龙源环保工程有限公司，江苏龙源催化剂有限公司，
类型：发明
国别省市：北京,11