一种甲基乙烯基聚硅氧烷‑生物可降解聚酯嵌段共聚物制造技术
A methyl vinyl polysiloxane biodegradable polyester copolymer
The invention provides a methyl vinyl polysiloxane biodegradable polyester (PCL PMVS PCL) block copolymers with methyl vinyl hydroxyl polysiloxane (PMVS) as the initiator, caused by the ring opening polymerization reaction of biodegradable polyester monomers in the presence of catalyst, methyl vinyl polysiloxane biodegradable polyester copolymer. The present invention first introduced hydroxyl methyl vinyl polysiloxane in biodegradable polyester backbone, the methyl vinyl polysiloxane biodegradable polyester copolymer can be compatible with other polyester blend well. Due to the excellent flexibility and mechanical properties of methyl vinyl poly (vinyl silicate) in chain segments, they can be used as toughening agents for biodegradable polyesters such as polylactic acid and poly (acetic acid). At the same time, the carried ethylene provides more possibilities for cross-linking and functionalization.
【技术实现步骤摘要】
一种甲基乙烯基聚硅氧烷-生物可降解聚酯嵌段共聚物
本专利技术涉及生物可降解高分子材料领域，特别涉及一种甲基乙烯基聚硅氧烷-生物可降解聚酯嵌段共聚物。
技术介绍
生物可降解聚酯具有良好的生物相容性与可降解性，因此其在药物载体和组织工程等生物医学、工程塑料等领域获得广泛关注。但由于生物可降解聚酯脆性高、硬度大等因素使其应用范围受到限制，单纯的生物可降解聚酯已经不能满足人们对其使用的需求。端羟基聚硅氧烷是重要的有机硅中间体，利用羟基与其他基团的反应可将聚硅氧烷引入相应聚合物结构中，提高后者的柔韧性、耐热性、耐寒性和透光性等。与端羟基甲基聚硅氧烷相比，端羟基甲基乙烯基聚硅氧烷含有乙烯基，不但能赋予改性聚合物更优异的耐高温性能和耐辐射性能，而且更重要的是可以进行聚合物的功能化，进而扩大其应用范围。本专利技术在生物可降解聚酯主链中引入了甲基乙烯基聚硅氧烷
技术实现思路
本专利技术的目的是提供一种新型含有乙烯基的聚硅氧烷-生物可降解聚酯嵌段共聚物，使合成的聚硅氧烷-生物可降解聚酯嵌段共聚物不仅保存了原有生物可降解聚酯的优良性能，而且可以有效改善材料的柔韧性、耐热性等，双键的存在为材...
【技术保护点】
一种甲基乙烯基聚硅氧烷‑生物可降解聚酯嵌段共聚物，其特征在于，所述聚硅氧烷为甲基乙烯基羟基聚硅氧烷，通过活性端羟基在催化剂的条件下引发生物可降解聚酯开环聚合形成嵌段共聚物。
【技术特征摘要】
1.一种甲基乙烯基聚硅氧烷-生物可降解聚酯嵌段共聚物，其特征在于，所述聚硅氧烷为甲基乙烯基羟基聚硅氧烷，通过活性端羟基在催化剂的条件下引发生物可降解聚酯开环聚合形成嵌段共聚物。2.如权利要求1所述的一种甲基乙烯基聚硅氧烷-生物可降解聚酯嵌段共聚物，其特征在于，该化合物上带有-Si-O-Si-键和双键，不仅为产物提供柔韧性和耐高低...
【专利技术属性】
技术研发人员：宋晓峰，任亚君，郭慧玲，张雪，崔心想，
申请(专利权)人：长春工业大学，
类型：发明
国别省市：吉林,22