一种贵金属多孔纳米膜及其制备方法技术
Noble metal porous nano film and preparation method thereof
The present invention relates to a noble metal nano porous film and its preparation method, the noble metal nano porous membrane by particle size is 5 ~ 20nm of noble metal nanoparticles assembled with small noble metal nanoparticles, the diameter of 1 to 10nm, the noble metal nano porous film thickness is 0.2 ~ 1 m. The preparation method is as follows: 1) the noble metal precursors and surfactants dissolved in water to obtain the precursor solution; 2) the precursor solution is heated to boiling, bubbles to the precursor solution when adding reducing agent, and continue to gather a layer of clear films at the water air interface is heated until 3) nanoparticles; separating film, noble metal nano porous film. The noble metal porous nanometer membrane obtained by the invention has good catalytic activity and stability.
【技术实现步骤摘要】
一种贵金属多孔纳米膜及其制备方法
本专利技术涉及纳米材料
，具体涉及一种贵金属多孔纳米膜及其制备方法。
技术介绍
贵金属材料具有独特的热、电、磁和光等性能，使其在能源、化工、催化、生物传感等领域有着广泛的应用前景。然而，由于贵金属资源有限，成本较高，因此在实际应用中减少贵金属的用量至关重要。理论和实验结果表面，贵金属材料的性质高度依赖于它的结构。在具体的催化过程中，贵金属材料的高效性和选择性能够通过控制贵金属的结构来得以优化，使贵金属催化剂获得理想的结构，就能极大地提升贵金属材料的催化性能和催化效率。贵金属纳米材料是目前研究的热门课题。贵金属纳米粒子由于具有小尺寸效应，比表面积较大，因此具有较高的催化活性。但是由于其比表面能较高，因而容易团聚，导致其性能下降。因此，将贵金属制成薄膜材料能够显著地提高贵金属纳米颗粒的形态稳定性，并且具有宏观可操作性。而进一步将贵金属制成多孔薄膜结构，可以提升贵金属材料的活性比表面积，从而提升其性能。尽管目前合成薄膜材料和多孔材料方法繁多，但大多工艺繁琐、耗时较长，或涉及有机溶剂。本专利技术提供了一种在水-空气界面上进行自组装合...
【技术保护点】
一种贵金属多孔纳米膜，其特征在于，所述贵金属多孔纳米膜由粒径为5～20nm的贵金属纳米粒子组装而成，贵金属纳米粒子间具有小孔，孔径为1～10nm，所述贵金属多孔纳米膜厚度为0.2～1μm。
【技术特征摘要】
1.一种贵金属多孔纳米膜，其特征在于，所述贵金属多孔纳米膜由粒径为5～20nm的贵金属纳米粒子组装而成，贵金属纳米粒子间具有小孔，孔径为1～10nm，所述贵金属多孔纳米膜厚度为0.2～1μm。2.根据权利要求1所述的贵金属多孔纳米膜，其特征在于：所述贵金属纳米粒子为金纳米粒子、银纳米粒子、铂纳米粒子、钯纳米粒子中的一种，或者金纳米粒子与银纳米粒子的混合物，或者铂纳米粒子与钯纳米粒子的混合物。3.一种权利要求1-2任一所述的贵金属多孔纳米膜的制备方法，其特征在于步骤如下：1)将贵金属前驱物及表面活性剂按摩尔比1:3溶解于水中，得到前驱体溶液；2)将步骤1)所得前驱体溶液加热至沸腾，待前驱体溶液中产生气泡时加入还原剂，其中摩尔比还原剂：贵金属前驱物＝10:1，并持续加热直至纳米粒子在水-空气界面上聚集成一层明显的薄膜；3)将步骤2)...
【专利技术属性】
技术研发人员：阳晓宇，肖宇轩，应杰，魏浩，范思宇，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。