The invention discloses a welding process of powder metallurgy and the 1215 steel pipe bracket, which comprises the following steps: powder metallurgy steel bracket and 1215 interference fit joint with solder paste on the rack and fittings; the powder metallurgy bracket and 1215 tube into the oven, after a period of time after the removal of welding parts, through tensile test the welding strength is effective, the leak test confirmed the welding sealing effect. The present invention provides a welding process that makes the sealing joint of powder metallurgy parts and 1215 steel tubes firm and can be produced in batches.
【技术实现步骤摘要】
粉末冶金支架和1215钢管的焊接工艺
本专利技术涉及一种焊接工艺，具体涉及一种粉末冶金支架和1215钢管的焊接工艺。
技术介绍
如今，粉末冶金件适合于批量生产，适合于切削少的机械零件，节能，节材，无污染。粉末冶金件与其他件的连接运用也普遍化.由于粉末冶金制作工艺导致了其必然内部必然存在孔隙，从而影响热导率，热膨胀，淬火性，使焊接失效。
技术实现思路
专利技术目的：本专利技术针对现有技术中的不足，提出一种提高产品质量、减少报废率的粉末冶金支架和1215钢管的焊接工艺。技术方案：本专利技术所述的一种粉末冶金支架和1215钢管的焊接工艺，包括如下步骤：A、粉末冶金支架和1215钢管过盈配合；B、在粉末冶金支架和1215钢管接合处涂焊膏；C、将粉末冶金支架和1215管放入钎焊炉；D、通过抗拉强度的检测验证焊接是否有效；E、通过检漏测试确认焊接密封的效果。进一步的，步骤（B）所述的焊膏的组分配比为：紫铜：镍：锰=60％：30％：10％。进一步的，步骤（C）所述钎焊炉的温度设置为：预热400-500℃，加热室900℃，逐步升到1100℃，20分钟后，温度到100-200℃，再冷却...
【技术保护点】
一种粉末冶金支架和1215钢管的焊接工艺，其特征在于：包括如下步骤：A、粉末冶金支架和1215钢管过盈配合；B、在粉末冶金支架和1215钢管接合处涂焊膏；C、将粉末冶金支架和1215管放入钎焊炉；D、通过抗拉强度的检测验证焊接是否有效；E、通过检漏测试确认焊接密封的效果。
【技术特征摘要】
1.一种粉末冶金支架和1215钢管的焊接工艺，其特征在于：包括如下步骤：A、粉末冶金支架和1215钢管过盈配合；B、在粉末冶金支架和1215钢管接合处涂焊膏；C、将粉末冶金支架和1215管放入钎焊炉；D、通过抗拉强度的检测验证焊接是否有效；E、通过检漏测试确认焊接密封的效果。2.根据权利要求1所述的一种粉末冶金支架和1215钢管的焊...
【专利技术属性】
技术研发人员：赵郁鎏，童日光，
申请(专利权)人：广东鸿图南通压铸有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。