一种催化氧化NO的催化剂及其制备方法和应用技术

本发明专利技术公开了一种催化氧化NO的催化剂及其制备方法和应用，该催化剂包括载体氮掺杂铈锆固溶体和活性组分氧化铬，所述氮掺杂铈锆固溶体载体中铈和锆的摩尔比为0.25:1，所述氧化铬中的铬元素与氮掺杂铈锆固溶体载体的质量比为1:10。本发明专利技术的催化剂具有较高的催化氧化NO的活性，同时该催化剂在含较高浓度的SO

Catalyst for catalytic oxidation of NO, preparation method and application thereof

The invention discloses a NO catalytic oxidation catalyst and preparation method and application thereof, the catalyst comprises a carrier of nitrogen doped ceria zirconia and active component of chromium oxide, the molar ratio of the nitrogen doped ceria zirconia solid solution of cerium and zirconium bulk carrier is 0.25:1, the quality of the element chromium in chromium oxide with nitrogen doped ceria zirconia carrier is 1:10. The catalyst of the present invention has a high catalytic activity for oxidation of NO, and at the same time, the catalyst has a higher concentration of SO

【技术实现步骤摘要】
一种催化氧化NO的催化剂及其制备方法和应用
本专利技术涉及燃煤烟气脱硝
，具体说是一种催化氧化NO的催化剂及其制备方法和应用。
技术介绍
二氧化硫(SO2)和氮氧化物(NOx)是目前仅次于颗粒物的主要大气污染物，对人体健康和自然环境危害严重。燃煤是造成SO2和NOx污染的主要原因，本世纪以来，国家大力发展烟气脱硫，SO2控制技术日益成熟，因而NOx脱除便逐渐成为人们研究热点。目前，国内外普遍采用选择性催化还原(SCR)技术对NOx进行控制。SCR技术具有污染物去除率高、技术成熟的优点，但同时也存在氨逃逸、原子不经济等不足。此外2016年1月1日修订实施的《大气污染防治法》对SO2、NOx等污染物提出了更严格的排放标准，因此开发高效、低成本的脱硝技术以满足超低排放的标准具有重要的意义和广阔的应用前景。NOx主要以NO(>95%)的形式存在，因此要实现低成本烟气脱硝，最简便的方法是将不溶于水的NO部分氧化为NO2，再用碱液吸收湿法脱除，其中氧化率(NO2/NOx)达到50%左右时可实现最大的吸收率。目前主要有等离子体氧化法、氧化剂(ClO2、O3、KMnO4或H2O2等)氧化本文档来自技高网...

【技术保护点】
一种催化氧化NO的催化剂，其特征在于，该催化剂包括载体氮掺杂铈锆固溶体和活性组分氧化铬，所述氮掺杂铈锆固溶体载体中铈和锆的摩尔比为0.25:1，所述氧化铬中的铬元素与氮掺杂铈锆固溶体载体的质量比为1:10。

【技术特征摘要】
1.一种催化氧化NO的催化剂，其特征在于，该催化剂包括载体氮掺杂铈锆固溶体和活性组分氧化铬，所述氮掺杂铈锆固溶体载体中铈和锆的摩尔比为0.25:1，所述氧化铬中的铬元素与氮掺杂铈锆固溶体载体的质量比为1:10。2.权利要求1所述的催化氧化NO的催化剂的制备方法，其特征在于，具体步骤如下：1）按照铈和锆的摩尔比0.25:1的比例称取硝酸铈和氧氯化锆，将硝酸铈和氧氯化锆溶于去离子水中，经常温搅拌、恒温水浴、烘干、煅烧、研磨得到铈锆固溶体粉末；2）将步骤一得到的铈锆固溶体粉末置于气氛炉中，保持氨气气氛，进行高温处理，降温后得到氮掺杂铈锆固溶体粉末，其中氨气气氛的浓度为1~100%，高温处理温度为600~1000℃，高温处理时间为8~12小时；3）按照铬元素与氮掺杂铈锆固溶体的质量比为1：10的比...

【专利技术属性】
技术研发人员：蔡炜，陈敏东，钟秦，赵云霞，
申请(专利权)人：南京信息工程大学，
类型：发明
国别省市：江苏,32