一种磁性多孔高分子微球的制备方法技术

本发明专利技术公开了一种磁性多孔高分子微球的制备方法。本发明专利技术采用油酸包裹磁性三氧化二铁纳米粒子，再将磁性纳米粒子溶胀进甲基丙烯酸缩水甘油酯和乙二醇二甲基丙烯酸酯交联的多孔高分子微球的孔道中，得到磁性多孔高分子微球。本发明专利技术特点是以多孔高分子微球为模板，产品参数可控，工艺操作简单易行，原料成本低廉，操作简便，易于工业化实施。

Method for preparing magnetic porous polymer microsphere

The invention discloses a preparation method of a magnetic porous polymer microsphere. The invention adopts the oleic acid coated magnetic ferric oxide nanoparticles, and the porous polymer microspheres with magnetic nanoparticles swelling into glycidyl methacrylate and ethylene glycol methacrylate crosslinked two channels, magnetic porous polymer microspheres were obtained. The invention is characterized in that the porous polymer microsphere is used as a template, the product parameter is controllable, the process operation is simple and easy, the raw material cost is low, the operation is simple, and the industrialization is easy to implement.

【技术实现步骤摘要】
一种磁性多孔高分子微球的制备方法
本专利技术涉及磁性微球
，尤其涉及一种磁性多孔高分子微球的制备方法。
技术介绍
聚合物磁性纳米微球是新型功能性复合材料。一方面由于具有磁性纳米粒子的磁导向性，聚合物磁性纳米微球可随外加磁场变化而运动，从而实现与体系的快速分离；另一方面聚合物磁性微球具有的有机表面，可通过丰富的化学反应进行表面改性，而在微球表面引入富含各种功能性的基团而使其具有不同的表面功能与反应活性。聚合物磁性纳米微球因具有良好的小尺寸效应、量子尺寸效应、表面效应和磁学特性，加之高分子材料本身柔软、稳定、易加工等基本特点，而成为当今国内外学者研究磁性功能材料的热点，且已经被广泛应用于生化分离、催化、医学、环境等领域。制备聚合物磁性纳米微球的方法一般可分为一步法和二步法：一步法是在成球前即加入磁性纳米材料，成球时聚合物将其包裹于其中；二步法是先制备非磁性小球，然后通过处理使磁性材料进入其中，最后磁性纳米粒子以分散的形式存在于微球的骨架材料中。一步法虽发展较早，应用比较广泛，但从现有的报道看，反应条件相对苛刻、产量过低，且磁性复合微球中的功能基团的含量偏少，磁含量不高，阻碍了高分子本文档来自技高网...

【技术保护点】
一种磁性多孔高分子微球的制备方法，其特征在于，所述方法采用模板法结合边溶胀边聚合法制备磁性多孔微球。

【技术特征摘要】
1.一种磁性多孔高分子微球的制备方法，其特征在于，所述方法采用模板法结合边溶胀边聚合法制备磁性多孔微球。2.根据权利要求1所述的制备方法，其特征在于，所述方法包括采用油酸包裹磁性三氧化二铁纳米粒子，再将所述磁性纳米粒子溶胀进甲基丙烯酸缩水甘油酯和乙二醇二甲基丙烯酸酯交联的多孔高分子微球的孔道中，得到所述磁性多孔高分子微球。3.根据权利要求2所述的制备方法，其特征在于，所述磁性多孔高分子微球的粒径为1μm-8μm。4.根据权利要求1所述的制备方法，其特征在于，所述方法中的油相包括四氢呋喃、正己烷；水相包括...

【专利技术属性】
技术研发人员：王勇，朱丽丽，滕超，任连兵，陈继伟，洪梅，
申请(专利权)人：北京大学深圳研究生院，
类型：发明
国别省市：广东,44