本发明专利技术涉及一种高容量安全的导电高聚物包覆硫电极材料及其制造方法，为改善单质硫作为电极活性物质的导电性和使用寿命，在制备过程采用了雾化喷雾预处理：对聚合反应的前驱物进行预处理，首先细化反应物的颗粒然后再进行吡咯聚合，对细化后硫颗粒表面进行包覆修饰，从而极大地提高了正极材料的导电性、改善了整个电池的容量及循环寿命。

High capacity safety conductive polymer coated sulfur electrode material and manufacturing method thereof

The invention relates to a conductive polymer high capacity safety coated sulfur electrode material and its manufacturing method, in order to improve the sulfur as a conductive electrode active material and the service life, in the preparation process of the spray pretreatment: the precursor polymerization pretreatment, the first reactant particles and then refined after the refinement of pyrrole polymerization, sulfur particles surface coating modification, thereby greatly improving the cathode conductivity, improve the capacity and cycle life of the battery.

【技术实现步骤摘要】
一种高容量安全的导电高聚物包覆硫电极材料及其制造方法
本专利技术涉及可充电锂离子电池
，特别是一种高容量安全的导电高聚物包覆硫电极材料及其制造方法。
技术介绍
锂离子电池作为商品已经日趋成熟，同时也是当今电动车驱动能源的首选。目前锂离子电池的容量主要受限于电池的正、负极材料的比容量，即，正、负极材料可储存锂量的多少。从电极材料的研究进展看正极材料的比容量还是落后于负极材料，很多负极材料的比容量已超过了1,000毫安时/克，例如：具有高导电性的金属锗的理论比容量达到1,600毫安时/克(也是最具吸引力的负极材料之一)。近年来，把硫作为可充锂电池中的正极材料的倍受重视，因为单质硫作为锂-硫二次电池的正极材料其理论比容量高达1672毫安时/克，功率密度达到2600瓦时/公斤，远高于目前已经商业化的钴酸锂/石墨锂离理论子电池(其理论能量密度360瓦时/公斤)同，时单质硫的价格低廉、产量丰富、安全无毒、环境友好。因此锂-硫电池体系被认为是最具希望的新一代高容量动力锂离子电池。锂-硫电池体系虽然具有上述的优点，但面临着必须要解决的问题:如采用100％硫元素作为正极材料，由于硫本身具有的非导本文档来自技高网...

【技术保护点】
一种高容量安全的导电高聚物包覆硫电极材料，其特征在于：它以活性炭和导电聚吡咯作为硫电极材料的包覆层，包覆层在硫颗粒的表面。

【技术特征摘要】
1.一种高容量安全的导电高聚物包覆硫电极材料，其特征在于：它以活性炭和导电聚吡咯作为硫电极材料的包覆层，包覆层在硫颗粒的表面。2.根据权利要求1所述的高容量安全的导电高聚物包覆硫电极材料，其特征在于：采用雾化喷雾技术，在包覆前对活性炭和硫进行预处理、先得到细化的活性炭-硫混合粉末，然后进行活性炭-硫-聚吡咯的聚合反应，使导电高聚物聚吡咯包覆层与被包覆的活性炭-硫颗粒之间形成固-固面,可以有效地防止硫离子从被包覆的硫电极中析出进入有机电解液中，因而提高了电池的循环寿命。3.根据权利要求2所述的高容量安全的导电高聚物包覆硫电极材料，其特征在于：经过喷雾雾化处理，达到细化的活性炭-硫粉末，其粒度大小可以控制在：0.1μm～10μm。4.根据权利要求1所述的高容量安全的导电高聚物包覆硫电极材料，其特征在于：所述的包覆层与...