The present invention relates to the technical field of resistance paste, especially a buried resistor paste, in accordance with the mass fraction meter comprises the following components: linear phenolic resin 5-13, conductive graphite 3-9, butyl phosphoric acid three 12-18, three 2.6-5.4 propylene glycol ether, polyethylene terephthalate, 3.2-6.8, ethoxylated alkyl phenol amine 3-12, ortho methyl phenolic epoxy resin 15-23, ceramic powder 22-30 parts. Using the above formula, the invention realizes embedded resistance paste, flame retardant, heat resistance, aging, thermal radiation, environmental protection and other complex functions, and improve the stability of the system; in addition, the invention of low cost components, convenient popularization and application.
【技术实现步骤摘要】
一种内埋电阻浆料
本专利技术涉及电阻浆料
,特别是一种内埋电阻浆料。
技术介绍
现在有的已采用化学稳定性更高的金属及其硫化物和高分子有机化合物作为导电相。分为银钯浆料、二氧化钌浆料、钌酸盐浆料以及铱和铑的浆料。其中以钌系浆料应用最多。它们具有很好的化学稳定性、热稳定性和耐湿性、电阻值精度高范围宽、电阻温度系数小、高阻噪音低、与银基导带兼容性好。
技术实现思路
本专利技术需要解决的技术问题是提供一种内埋电阻浆料。为解决上述的技术问题,本专利技术的一种内埋电阻浆料,按照质量份数计包括以下组分:线性酚醛树脂5-13份,导电相石墨粉3-9份,磷酸三丁酯12-18份,三丙二醇甲醚2.6-5.4份,聚对苯二甲酸乙二醇酯3.2-6.8份,乙氧基化烷基酚胺3-12份,邻甲基酚醛环氧树脂15-23份,陶瓷粉22-30份。进一步的,按照质量份数计包括以下组分:线性酚醛树脂5份,导电相石墨粉3份,磷酸三丁酯12份,三丙二醇甲醚2.6份,聚对苯二甲酸乙二醇酯3.2份,乙氧基化烷基酚胺3份,邻甲基酚醛环氧树脂15份,陶瓷粉22份。进一步的,按照质量份数计包括以下组分:线性酚醛树脂13份,导电相石墨粉9份,磷酸三丁酯18份,三丙二醇甲醚5.4份,聚对苯二甲酸乙二醇酯6.8份,乙氧基化烷基酚胺12份,邻甲基酚醛环氧树脂23份,陶瓷粉30份。进一步的,按照质量份数计包括以下组分:线性酚醛树脂8份,导电相石墨粉5份,磷酸三丁酯13份,三丙二醇甲醚3.3份,聚对苯二甲酸乙二醇酯4.9份,乙氧基化烷基酚胺6份,邻甲基酚醛环氧树脂18份,陶瓷粉25份。进一步的,按照质量份数计包括以下组分:线性 ...
【技术保护点】
一种内埋电阻浆料,其特征在于,按照质量份数计包括以下组分:线性酚醛树脂5‑13份,导电相石墨粉3‑9份,磷酸三丁酯12‑18份,三丙二醇甲醚2.6‑5.4份,聚对苯二甲酸乙二醇酯3.2‑6.8份,乙氧基化烷基酚胺3‑12份,邻甲基酚醛环氧树脂15‑23份,陶瓷粉22‑30份。
【技术特征摘要】
1.一种内埋电阻浆料,其特征在于,按照质量份数计包括以下组分:线性酚醛树脂5-13份,导电相石墨粉3-9份,磷酸三丁酯12-18份,三丙二醇甲醚2.6-5.4份,聚对苯二甲酸乙二醇酯3.2-6.8份,乙氧基化烷基酚胺3-12份,邻甲基酚醛环氧树脂15-23份,陶瓷粉22-30份。2.按照权利要求1所述的一种内埋电阻浆料,其特征在于,按照质量份数计包括以下组分:线性酚醛树脂5份,导电相石墨粉3份,磷酸三丁酯12份,三丙二醇甲醚2.6份,聚对苯二甲酸乙二醇酯3.2份,乙氧基化烷基酚胺3份,邻甲基酚醛环氧树脂15份,陶瓷粉22份。3.按照权利要求1所述的一种内埋电阻浆料,其特征在于,按照质量份数计包括以下组分:线性酚醛树脂13份,导电相石墨...