The present invention provides a method for the synthesis of nano mullite powder Mo, this method is based on China's abundant natural bauxite as raw material, after 800 ~ 1200 DEG C roasting, hydrothermal synthesis of mullite nano powder. The invention has the advantages of cheap raw material, low reaction temperature, simple method and low production cost. The obtained mullite has higher purity, and the content is higher than 80%; the powder agglomerate is small, and the powder grain is less than 40nm, and the particle size of the two times is less than 200nm. The mullite powder rice flour prepared by the invention has good performance and can be widely used in metallurgy, ceramics, electronics and many other fields. The invention can greatly increase the added value of alumina products and reduce the preparation cost of mullite nanometer powder.
【技术实现步骤摘要】
所属领域本专利技术涉及一种陶瓷粉料的制备方法，具体涉及到一种由铝矾土水热合成莫来石纳米粉体的制备方法。
技术介绍
莫来石本身具有许多优良物理特性，如低膨胀系数、低热导、低蠕变、低介电常数、高耐热冲击和高温强度等。莫来石的这些特性使得其在耐火材料、高温结构材料、微电子封装材料、光学材料及介电和高温保护涂层等众多领域中得到广泛应用，有着重要的工业价值。而纳米粉体由于尺寸小，表面原子占相当大的比例，因而表面能高，具有高的活性，其熔点和烧结温度较常规粉体低得多；将其作为添加剂引入到耐火材料、高温结构材料中，可望改善其烧结性能和显微结构，从而强烈地影响该类材料的力学性能。在耐火材料工业中所使用的莫来石熟料，大多是以天然矿物为原料，采用烧结法和电熔法合成的。常见的天然矿物原料有特级生焦宝石、矾土精料、苏州土、高岭石、煤歼石，以及蓝晶石、红柱石、矽线石等。为了调节原料的Al2O3/SiO2比例，一般采用加入石英粉、工业氧化铝或其中间产品氢氧化铝等办法。用天然原料合成莫来石的工艺流程随所用原料不同而有较大变化，但一般可分为两大类，即湿法和干法(钟香崇《中国耐火原料的发展.硅酸盐通报...
【技术保护点】
矾土基莫来石纳米粉体的制备方法，以高铝矾土、莫来石晶种为主要原料，采用水热法制备工艺，其特征在于：ａ．将高铝矾土与盐酸和硫酸的混合酸溶液或浓度为１０－３６％的盐酸溶液混合，在搅拌下加热至４０－８０℃，恒温１－１０小时，静置１－３天，然后用水充分洗涤、抽滤、烘干；ｂ．将酸洗除铁后的高铝矾土９５－１００份？、莫来石晶种１－５份，共磨１－２小时，然后在５００－６００℃下预焙烧１－３小时，再经８００－１２００℃焙烧２－８小时，磨细；ｃ．将焙烧后的高铝矾土３－７份，配以适量矿化剂、１００份溶剂，再加入０．１－０．４份分散剂，充分搅拌后放入高压釜中，升温至１００－２００℃，保温２－１０...
【技术特征摘要】
【专利技术属性】
技术研发人员：钟香崇，贾晓林，叶方保，
申请(专利权)人：郑州大学，
类型：发明
国别省市：41[中国|河南]