一种清水自密实混凝土拌合物，按照重量组分配比组成，其中，水泥为１、水为０．２８～０．３５、砂子为２．７８～４．１８、石子为２．７８～４．１８、粉煤灰为０．３４～１、矿渣粉０．３４～１、聚羧酸高效减水剂为０．０２１～０．０４３。本发明专利技术优点是：混凝土拌合物具有高抗离析性、不泌水，又具有高流动性，能自行流注充填模板而浇注成形，获得高质量密实混凝土，且在施工方使用清水模板的情况下混凝土表面光滑，颜色均匀一致，视觉效果较好；硬化后混凝土力学性能和耐久性能优良，抗压强度达到５０ＭＰａ以上，大量使用工业废料，混凝土成型后表面可直接作为建筑物外饰面，其具有凝重素雅的质感、独特的视觉效果，且可节省二次装修的费用。

Clear water self compacting concrete mixture

A water self compacting concrete mixture, according to the weight ratio, the cement is 1, water is 0.28 ~ 0.35, 2.78 ~ 4.18 sand and gravel is 2.78 ~ 4.18, 0.34 ~ 1 of fly ash and slag powder of 0.34 ~ 1, polycarboxylate superplasticizer is 0.021 ~ 0.043. The invention has the advantages that the concrete mixture has high anti segregation and bleeding, but also has high mobility, self filling templates and streamer casting, high quality concrete, smooth surface and concrete in the construction of water using a template, color uniform, good visual effect after hardening performance; the mechanical properties of concrete and excellent durability, compressive strength can reach more than 50MPa, the extensive use of industrial waste, after forming of concrete surface can be directly used as a building with visual effect, its dignified elegance texture, unique, and can save two times the cost of renovation.

【技术实现步骤摘要】

【技术保护点】
一种清水自密实混凝土拌合物，按照重量组分配比组成，其中，水泥为１、水为０．２８～０．３５、砂子为２．７８～４．１８、石子为２．７８～４．１８、粉煤灰为０．３４～１、矿渣粉０．３４～１、聚羧酸高效减水剂为０．０２１～０．０４３。

【技术特征摘要】

【专利技术属性】
技术研发人员：孙志强，郑子明，翟丽娟，
申请(专利权)人：北京浩然混凝土有限公司，
类型：发明
国别省市：11[中国|北京]