The invention relates to a nanometer heat energy particle catalytic heat accumulating refractory material, belonging to the catalytic combustion material. Al: 2 O: 3 - 100, BaO2 - 6, K: 2 O4 ~ 7, MgO1 ~ 4, CaO0.5 ~ 4, SrO0.5 ~ 1, TiO0.1 ~ 0.3, 20 to 35 parts of water. According to the formula of mixing raw materials, stirring, using high speed dispersion machine with 1700 ~ 2000 rpm / min stirring for 1 to 3 hours; the mixture into a mould, press in 5 ~ 10MPa pressure 10 ~ 20 minutes at room temperature, natural drying or by drying machine with 30 to 60 DEG C dried, cooled to 1000 to 1300 DEG C in calcining kiln, remove. The utility model has the advantages that the activated carbon gas can be activated and burned by the active gas under catalysis, so as to achieve the purpose of energy saving. It can be used as thermal insulation material in high, medium and low temperature equipment. This product can be widely used in various related fields.
【技术实现步骤摘要】
本专利技术属于催化燃烧材料，适合于高温、中温和低温催化燃烧。
技术介绍
目前燃烧领域中的火焰燃烧匀是以自然及强制机械化的气态明火燃烧，对于火焰的催化燃烧尚属研究阶段，特别是高、中、低温的活性可燃性气体没有再进一步催化燃烧。而造成能量的无效排放，造成能源浪费。目前国内外的催化燃烧还只是在高档汽车的尾部排烟、及有机废气催化燃烧中应用，目前对工业电站锅炉、工业锅炉、工业窑炉和民用燃烧领域均无应用；特别是现有催化燃烧材料的制作工艺复杂、材料成本高，普通企业无法应用。
技术实现思路
本专利技术提供一种纳米光能粒子催化蓄热耐火材料，以解决目前催化燃烧材料存在的制作工艺复杂、材料成本高，普通企业无法应用的问题。本专利技术采取的技术方案是包括下列按重量份数比的原料Al2O3100份BaO 2～6份把La2O3制成粒径0.005微米以下的粉料，加入水，搅拌，密度为1.05g/cm3；0.5～0.8份把Nd2O3制成粒径0.005微米以下的粉料，加入水，搅拌，密度为1.03g/cm3；0.5～0.8份K2O 4～7份MgO 1～4份CaO 0.5～4份SrO 0.5～...
【技术保护点】
一种纳米光能粒子催化蓄热耐火材料，其特征在于包括下列按重量份数比的原料：Ａｌ↓［２］Ｏ↓［３］１００份，ＢａＯ２～６份，把Ｌａ↓［２］Ｏ↓［３］制成粒径０．００５微米以下的粉料，加入水，搅拌，密度为１．０５ｇ／ｃｍ↑［３］；０．５～０．８份，把Ｎｄ↓［２］Ｏ↓［３］制成粒径０．００５微米以下的粉料，加入水，搅拌，密度为１．０３ｇ／ｃｍ↑［３］；０．５～０．８份，Ｋ↓［２］Ｏ４～７份，ＭｇＯ１～４份，ＣａＯ０．５～４份，ＳｒＯ０．５～１份，ＴｉＯ０．１～０．３份，水２０～３５份。
【技术特征摘要】