A method for producing glass beads, the refractive index is 1.5 ~ 1.55 of the broken glass production of glass beads, the use of methanol after cleaning, crushing into 16 ~ 500 mesh powder, then evenly added to the beads of flame, gas pressure is 0.08 ~ 0.15MPa, and rotating wind outlet in the gas nozzle with 50 ~ 100MPa, the glass powder in high speed rotating upward into the flame beads made of glass beads, according to the use of glass beads, screened different mesh glass beads, is finished, the advantage is that glass bead circle rate high, up to more than 90%, the refractive index can reach to 1.5 ~ 1.55, transparent and colorless, products, no air bubbles and impurities.
【技术实现步骤摘要】
本专利技术涉及。玻璃微珠是一种多用途产品，它在交通、机械加工及化工等生产领域广泛应用，例如，用玻璃微珠生产道路标志线或标志牌涂料，这种含有玻璃微珠的涂料可以使车灯的光源平行的反射回来，使司机看清前进的方向，提高夜间行车的安全性。在机械加工领域，玻璃微珠可以用于金属物的清理与抛光，作为喷丸或研磨材料，它具有化学稳定性好，使用时间长，可加速清理，及保持原物加工精度和光洁度等优点。在化工生产领域，玻璃微珠可用作塑料、橡胶、油漆及各种粘接胶的添加剂增强剂。因此，玻璃微珠是生产上述产品或加工方法的重要材料，玻璃微珠的技术性能对上述产品和加工方法具有直接的影响，是提高其质量的关键。现有技术中的玻璃微珠的生产方法主要包括原料选取、粉碎、高温制取微珠等工序，在原料粉碎后，玻璃粉末通常是直接加在成珠火焰上，在火焰的作用下形成玻璃微珠，而制取微珠的火焰是用天燃气作为燃料，直接在喷嘴上喷出形成的，由于天燃气本身的压力较低，所以，火焰向上运动的速度也较慢，而且，火焰是一直向上的，因此，形成的玻璃微珠存在着成圆率低、圆度差、玻璃微珠中含杂质多等问题，在一定程度上影响了玻璃微珠的应用。...
【技术保护点】
一种玻璃微珠的生产方法，其特征在于，它是按照下述方法生产的：１．１、原料选取：采用碎玻璃制取玻璃微珠，选取折射率为１．５～１．５５的碎玻璃作为原料；１．２、将折射率符合要求的碎玻璃用甲醇清洗，去除其中的杂质，然后，粉碎成１６～５００ 目的玻璃粉末；１．３、将玻璃粉末均匀的加入到玻璃微珠燃烧炉的成珠火焰上，火焰以天燃气为燃料，天燃气的压力为０．０８～０．１５ＭＰａ，并在天燃气喷嘴的出口处加上５０～１００ＭＰａ的旋转风，使玻璃粉末在高速旋转上升的成珠火焰中烧制成玻璃微珠 ；１．４、根据玻璃微珠的用途，筛选出不同目数的玻璃微珠，即为成品。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。