A foaming liquid glass forming process, which is characterized in that the glass material in the crucible with high melting temperature of about 1400 DEG C of the glass forming liquid evenly, when the temperature dropped to about 1300 degrees Celsius, the molten glass surface uniformly spread a thin layer of edible flour, stir quickly at the same time with an iron bar in fou after the crucible, crucible cover cover, about ten minutes after a foaming liquid glass can produce all kinds of vessels, its positive effect is: foam glass made by the invention of the bubble effect, uniform distribution of liquid glass does not appear waste problems.
【技术实现步骤摘要】
本专利技术涉及到发泡玻璃液的制作技术。有一种玻璃器皿其玻璃呈现气泡状态,而这种玻璃的形成通常是往熔化好的玻璃液中掺入一定量的碱或苏达来实现。其问题是以此形成的发泡玻璃液所做成的玻璃器皿其气泡的效果较差;另外所做成的玻璃器皿极易破碎;特别是发泡玻璃液中的气泡随着使用其制作玻璃器皿过程的变化,玻璃液中气泡的数量将随着时间增加而逐渐减少,这时如要达到人们满意的气泡量,就得往已加过碱或苏达的玻璃液中反复加入碱或苏达。这样势必使得玻璃液中碱或苏达的含量增加,从而将使得制作出来的玻璃器皿极易炸裂。本专利技术的目的是提供一种既能产生明显气泡效果的玻璃器皿,又能在反复加入形成气泡玻璃液的成份后,用其所制作的玻璃器皿的粹性不增加,也即不致造成玻璃料液浪废的问题发生的这么一种制作发泡玻璃液的制作技术。本专利技术的目的是这样实现的。一种发泡玻璃液的形成工艺,其特征在于将玻璃配合料在坩埚内经约1400℃左右的高温熔化形成均匀的玻璃液,当其温度降至约1300℃左右时,在玻璃液表面均匀地撒上一溥层食用面粉,与此同时迅速用铁棒将面粉搅入缶内,后用坩盖把坩口盖上约10分钟后即成为可制作各种形状发泡状玻璃器皿的发泡玻璃液。每次撒入的食用面粉量一般来说没有十分严格的规定,通常可取300~600g/次。铁棒将食用面粉搅入缶内的搅拌时间约在10~15分钟左右。本专利技术的积极效果1、由于食用面粉的成份不改变原玻璃液料中的成份比例,故避免了以往加碱或苏达使得玻璃器皿易碎或粹裂的问题,既使是反复加入,也不致造成玻璃料液的浪废。2、做成的发泡状玻璃器皿其气泡的效果明显,分布均匀。3、由于掺入的面 ...
【技术保护点】
一种发泡玻璃液形成工艺,其特征在于将玻璃配合料在坩埚内经约1400℃左右的高温熔化形成均匀的玻璃液,当其温度降至约1300℃左右时,在其玻璃液表面均匀地撒上一薄层食用面粉,与此同时迅速用铁棒搅入缶内,后用坩盖把坩口盖上,约10几分钟后即成为可制作各种器皿的发泡玻璃液。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。