A method for manufacturing a molded optical element, which comprises the following steps: A. preform, the glass preform nearly finished; B. fire will throw, the softening point of the pre implantation body press mold heating to the material above, let preform surface fine lines damage self repair; C. pressure. The preform fire thrown in one die out of two stage compression molding to achieve the target specifications; D. after annealing, the molding lens type and slow to make default temperature at room temperature in the mold, mold out finished lenses. Accordingly, it is possible to rapidly manufacture glass optical elements with high mirror quality of spherical surface, aspheric surface or special shape.
【技术实现步骤摘要】
本专利技术有关一种,尤指一种可用来制造高镜面精度的球面、非球面或特殊形状的玻璃光学元件,主要在同一模具内进行火抛、压造及退火的一贯工作,可使预形体表面的细微刮纷或凹点产生自我修复功能,以及可快速达成非球面镜或其它特殊镜片的制作;据以可增加该一产品的精密度及其经济价值。
技术介绍
一般现有玻璃光学元件(镜片)的制造方法,均经多次阶段研磨的方式制造而成,该现有以研磨方式的光学镜片,因为属接触性磨擦,故在其表面均会留下研磨痕迹,较严重的以肉眼都可以看的很清楚,导致该现有产品的品质难以控制,进而使制造成本也跟着提高。另外,以研磨方式制造光学镜片时,其对非球面或不对称形状的镜片的制造较为困难且无法达到预期的精确度,不只如此,即使针对一般曲率半径较小(即度数较大)的球面镜研磨,其在镜片的周缘亦容易造成曲率变形的情况;因此,该一现有的制造方法对一些特殊镜片的制造,并不是一个最好的方法,致对的实有改进必要。另外,目前在业界也有光学镜片以压造方式制造,其所使用的材料均以压克力材料或聚合物的树脂材料制成,致其所取得的成品(俗称塑料镜片)较易磨损,耐用性较差,同时其透光性也不如玻璃光学镜片,故其不适用于一些较精密的器械使用,且该一制造方法的制程也不适用于玻璃光学镜片使用。本案专利技术人有鉴于上述现有的以研磨方式制造光学镜片的缺点,以及以压造方式制造塑料镜片的方法不适于制造玻璃镜片使用,终专利技术出一种崭新的。
技术实现思路
本专利技术的主要目的在提供一种,其能有效且快速的修复以研磨方法制造的玻璃预形体表面所残留的磨改或细点,以可取得该光学镜片的最佳镜面精度。本专利技术的另一目的 ...
【技术保护点】
一种模造光学元件的制造方法,其特征在于,步骤包括有:a.预形体,先以研磨抛光方式制成极接近成品规格的玻璃预形体;b.火抛,将该预形体置入压造模具内加温至T↓[1]材料的软化点以上,让预形体表面的细纹损伤产生自我修复后,再降温 到压造时所需要的工作温度T↓[2];c.压造,在同一模具内使前一步骤降温至工作温度T↓[2]时而使其维持一段时间,并在该一时间内提供一作业压力P↓[1]作第一次加压成型到接近目标规格后,再使温度缓慢的降至退火温度T↓[3],并在降温 的初即骤升压力至P↓[2](大于P↓[1]以上)作第二次加压成型,以及在上述温度降至退火温度T↓[3]后,在此时将压力降至P↓[3](低于P↓[1])进行保压作业:d.退火,于完成第二次加压成型后让温度缓慢的下降至常温,以便开模取出 镜片,并在该退火过程的前段时间让模具压力下降至低于P↓[3]的状态,以使其内的光学镜片定型,以及在退火过程的后段时间则将压力完全释放。