The invention discloses a poly carboxylic acid water reducing agent, which is characterized in that: according to the quality of a project, including the following components: polyoxyethylene methyl vinyl ether 1800-2200, water 2800-3500, hydrogen peroxide 18-22, acrylic acid 100-180, ascorbic acid 8-12, 3-mercaptopropionic acid 8-12, sodium hydroxide 100-120 and silane 50-100. The poly carboxylate single methyl vinyl ether by agent prepared by the raw materials with the existing technology, unsaturated carboxylic acid, amide or anhydride, unsaturated sulfonate monomer material cost is low, the entire preparation process does not need too high temperature, low fuel cost the risk is small, and the preparation process, not the generation of other harmful gases, added to cement has the advantages of waterproof and anti collapse.
【技术实现步骤摘要】
本专利技术涉及聚羧酸减水剂的制作
,具体为一种聚羧酸减水剂及其制作工艺
技术介绍
混凝土外加剂是在混凝土搅拌过程中加入,用以改善新拌和硬化混凝土性能的物质,其掺量小于水泥重量的5%。聚羧酸高性能减水剂在混凝土中的掺量一般为0.18%(水泥重量),是混凝土外加剂中使用大、应用范围广的外加剂。它用于混凝土可实现下列目的:在混凝土和易性相同时,大幅度地降低混凝土用水量,可以提高混凝土强度;在混凝土水灰比相同时,可以大幅度地提高混凝土和易性;在混凝土和易性和强度相同的情况下,可以节约水泥用量的20-30%。聚羧酸高性能减水剂可直接用于混凝土,也可作各种不同功能外加剂的复配原料使用。
技术实现思路
本专利技术的目的在于提供一种聚羧酸减水剂,以解决上述
技术介绍
中提出的问题。为实现上述目的,本专利技术提供如下技术方案:一种聚羧酸减水剂,其特征在于:按质量份计,包括以下组分:优选的,质量份按照甲基烯基聚氧乙烯醚2000份,水3000份,双氧水20份,丙烯酸130份,抗坏血酸10份,巯基丙酸10份,氢氧化钠110份和硅烷80份配比出的聚羧酸减水剂性能最佳。聚羧酸减水剂的制作工艺如下:S1:采用重量份为50-100份的硅烷与重量份为1800-2200份的甲基烯基聚氧乙烯醚混合改性,改性的甲基烯基聚氧乙烯醚于45℃-55℃时投入聚合反应釜内,同时投入重量份为2800-3500份的水和重量份为1 ...
【技术保护点】
一种聚羧酸减水剂,其特征在于:按质量份计,包括以下组分:
【技术特征摘要】
1.一种聚羧酸减水剂,其特征在于:按质量份计,包括以下组分:
2.根据权利要求1所述的一种聚羧酸减水剂,其特征在于:质量份按照
甲基烯基聚氧乙烯醚2000份,水3000份,双氧水20份,丙烯酸130份,抗
坏血酸10份,巯基丙酸10份,氢氧化钠110份和硅烷80份配比出的聚羧酸
减水剂性能最佳。
3.一种权利要求1对所述的聚羧酸减水剂的制作工艺如下:
S1:采用重量份为50-100份的硅烷与重量份为1800-2200份的甲基烯基
聚氧乙烯醚混合改性,改...
【专利技术属性】
技术研发人员:史玉梅,
申请(专利权)人:青海金佳源建材有限公司,
类型:发明
国别省市:青海;63