The present invention relates to the technical field of concrete additives, especially a concrete superplasticizer; the concrete superplasticizer quality parts are as follows: 40 polycarboxylate superplasticizer liquor 45, polyethylene glycol 6 10 copies, 3.5 copies of the 2.5 zeolite powder and sodium stearate 4 6, two oxygen 3 Ti 7 and water 35 40; the invention of concrete superplasticizer has easily obtained raw materials, excellent characteristics and properties of low cost, through the reasonable collocation of components, with high admixture ratio and low cementitious material ratio as the main character; eventually work well high strength, good crack resistance, impermeability and long service life of concrete additives.
【技术实现步骤摘要】
一种混凝土缓凝减水剂
本专利技术涉及混凝土助剂
，尤其是一种混凝土缓凝减水剂。
技术介绍
众所周知，海底隧道的建设是目前交通建设中最为复杂、标准最高的施工项目；隧道混凝土不允许出现危害性裂缝，其最大埋入深度在-40m左右。海底隧道多采用工厂化预制全断面浇筑，一次浇筑混凝土方量达3400m3左右，设计强度为56d达到C50，同时为保证早龄期的拆模，要求3d强度达到C30。由于隧道混凝土结构需要长期承受高压海水作用，因此对隧道混凝土的抗渗性能、抗裂性能以及长期寿命提出了更高要求。目前常采用添加膨胀剂来提高混凝土的抗裂性能；大多是用煅烧高岭土、明矾石、地开石、铝矿渣、铝酸钙熟料或硫铝酸钙熟料与石膏配制的钙矾石类膨胀剂，存在膨胀能低、膨胀速率与混凝土凝结核水化反应速率不匹配、掺量大、碱含量高易引起碱骨料反应等不利因素；以CaO为主要成分的氧化钙类膨胀剂，存在膨胀速度过快、膨胀时间短、膨胀与混凝土收缩速率不协调、不易保存等缺点；以MgO为主要成分的氧化镁类膨胀剂，存在膨胀速度过慢，膨胀开始时间远落后于混凝土收缩开始时间，无法起到抗裂作用等弊端。
技术实现思路
本专利技术要解决的技术问题是：克服现有技术中的不足，提供一种性能稳定的混凝土缓凝减水剂。为解决上述技术问题，本专利技术采用的技术方案如下：一种混凝土缓凝减水剂，该混凝土缓凝减水剂的质量份组成如下：聚羧酸减水剂母液40-45份、聚乙二醇6-10份、沸石粉2.5-3.5份、硬脂酸钠4-6份、二氧化钛3-7份、水35-40份。作为优选，所述的一种混凝土缓凝减水剂，其特征在于：所述聚羧酸减水剂母液的固含量为38%。作...
【技术保护点】
一种混凝土缓凝减水剂，其特征在于，该混凝土缓凝减水剂的质量份组成如下：聚羧酸减水剂母液40‑45份、聚乙二醇6‑10份、沸石粉2.5‑3.5份、硬脂酸钠4‑6份、二氧化钛3‑7份、水35‑40份。
【技术特征摘要】
1.一种混凝土缓凝减水剂，其特征在于，该混凝土缓凝减水剂的质量份组成如下：聚羧酸减水剂母液40-45份、聚乙二醇6-10份、沸石粉2.5-3.5份、硬脂酸钠4-6份、二氧化钛3-7份、水35-40份。2.根据权利要求1中所述的一种混凝土缓凝减水剂，其特征在于：所述聚羧酸减水剂母液...