The present invention belongs to the field of Arts and crafts production, in particular to producing artificial stone by using blast furnace slag. The invention is characterized in that the raw materials for all or part of the blast furnace slag, iron oxide, potassium carbonate, sodium silicate, calcium carbonate, the preparation method comprises the following steps: weighing; crushing, grinding, mixing; stirring; melting; polishing, grinding and polishing. According to the artificial sun stone prepared by the invention can emit dazzling flash to the surrounding, delicate texture, luster and soft tenacity, has good mechanical properties, can be used in the production field of Arts and crafts, and has broad application prospects. The present invention uses blast furnace slag as raw material to produce products with high added value, realizes high added value of blast furnace slag, and opens up a new way for comprehensive utilization of industrial solid waste.
【技术实现步骤摘要】
本专利技术属于工艺品生产领域,具体说是利用炼铁过程中产生的工业固体废弃物——高炉渣生产的人造日光石及其制造方法。
技术介绍
高炉渣是炼铁生产过程中产生的工业固体废弃物,是我国排放量最多的工业固体废弃物之一,据统计,每炼1吨铁要产生0.3—1吨高炉渣。企业一般采用露天堆放的方式处理高炉渣,这一方面占用了大量土地,另一方面,高炉渣中的有害物质会污染周围的环境。多年来,人们采用了多种技术对高炉渣进行综合利用,如生产水泥和混凝土,或生产矿渣棉、微晶玻璃、农用肥料等,但这些技术均在一定程度上存在缺陷,如生产水泥和混凝土时,产品的力学性能指标不稳定,而且这些应用多数属于低附加值利用,产生的效益有限。基于上述原因,目前市场上迫切需要对高炉渣综合利用的新技术、新工艺。日光石是一种珍贵的宝石,它的内部含有一些特殊的矿物包裹体,从而会向周围发出耀眼的闪光,好像夜空中的星星一样,人们把这种现象称为“日光效应”,因此,这种宝石自古以来受到人们的喜爱。但是,天然的日光石储量很少,因而价格昂贵,不能满足普通消费者日益增长的需要。如果采用人工技术生产人造日光石,无疑具有重要的价值和意义。
技术实现思路
本专利技术的目的是克服传统的高炉渣综合利用技术存在的缺陷,以高炉渣为原料生产具有高附加值的产品——人造日光石,从而为高炉渣的综合利用开辟一条新的途径。本专利技术的特征是以高炉渣为主要原料,同时加入一定量的添加剂,经过称量、粉碎、研磨、混料、搅拌、熔炼、雕琢、打磨、抛光工艺制备人造日光石。本专利技术的制备方法为:1.人造 ...
【技术保护点】
1.一种人造日光石,其特征在于,其原料为高炉渣、三氧化二铁、碳酸钾、硅酸钠、碳酸钙中的全部或部分,其重量化学组成为:高炉渣:55-95%,三氧化二铁:1-20%,碳酸钾:5-45%,硅酸钠:5-45%,碳酸钙:5-25%。
【技术特征摘要】
1.一种人造日光石,其特征在于,其原料为高炉渣、三氧化二铁、碳酸钾、硅酸钠、碳酸钙中的全部或部分,其重量化学组成为:高炉渣:55-95%,三氧化二铁:1-20%,碳酸钾:5-45%,硅酸钠:5-45%,碳酸钙:5-25%。
2.根据权利要求1所述的人造日光石的制备方法,其特征在于它由下述步骤实现:
(1)按要求称量各种原料;
(2)将块状原料破碎、研磨;
(3)将各种原料...