A laser is suitable for mobile bed refining device double-layer cylindrical parts equipment welding method, the cross section of the net tube in triangular mesh perpendicular to the radial direction of the support ring is connected to form a mesh structure of staggered support ring, meshing with a laser wire slot angle and welding integrally formed on the support ring and then through the laser transmission welding; the outer cylinder and the inner cylinder net hole plate into a whole; can produce air tightness and stable support ring spacing cavity efficiently. Compared to the traditional winding resistance welding /TIG welding process for such products processing, the application has more high welding strength, reliable welding stability, quality more accurate seam gap and more beautiful, also can enlarge the production specifications, to meet the special requirements of some of the advantages of fluidized bed; at the same time due to the use of laser technology the production cost of water, electricity and other energy can be greatly reduced, in line with national current advocate of low-carbon, energy saving and environmental protection policy requirements.
【技术实现步骤摘要】
适用于流动床炼化装置双层筒状内件设备的激光焊接方法
本专利技术涉及大型流动床炼化装置双层筒状内件设备的激光焊接加工方法,具体地说是一种激光焊接制造V型丝网筒的外层孔板筒工装及其激光加工工艺。
技术介绍
流化床工艺是指反应过程中催化剂沿反应器轴向连续流动的一类化工技术,包括重整炼油、丙烷脱氢、苯乙烯等。其中重整炼油是生产高辛烷值汽油及轻芳烃的主要石油加工工艺;丙烷脱氢是生产现需求最重要的化工产品丙烯的工艺,其反应器网筒是当今炼油化工行业反应器内构件中结构最复杂,加工难度最高的产品之一;苯乙烯工艺采用乙苯催化脱氢制聚合单体。近年来此类化工项目在国内吸引了数千亿投资并呈扩大趋势。流化床装置中网筒结构内件设备是其核心部分之一,是指由倒三角形状的V型金属丝焊接而成的内构件,设计要求强度高,加工尺寸精确,焊接可靠,是反应器的核心设备。激光加工流化床装置网筒的过程中,用于固定网丝和支撑圈的工装设计极其重要:工装的设计制造不仅影响最终内层网筒尺寸和表面质量精度,而且还间接影响其焊接强度,如网丝与支撑圈之间接触不实易导致焊接热变形、表面开裂等缺陷。目前业内大多数制造商制造反应器V型丝网筒的通用工艺是先将三角形网丝与平直形支撑架的齿槽啮合,外层孔板筒工装采用分段式TIG填充氩弧焊用于紧固网丝与平直形支撑架,随后采用电阻焊焊成平板形网板,经冲压成所需弧形网板,再由多个弧板TIG焊接成圆形内层网筒,完成内构件制造。采用此加工工艺方法制造出的内构件由于数控冲压使网丝缝隙不均匀,网筒圆度差,变形难控制,焊后校形困难,内层网筒成形精度较差,效率较低,且合格率低,重新修复难度大;同时流化 ...
【技术保护点】
一种适用于流动床炼化装置双层筒状内件设备的激光焊接方法,其特征在于:所述方法将网筒中截面为三角形的网丝(1)垂直于支撑圈(2)的径向方向连接至支撑圈(2)上形成交错的网状结构,网丝(1)的一角与支撑圈(2)上的齿槽啮合并激光焊接形成整体;然后通过激光透射焊使外层孔板筒(3)与内层网筒成为一体;可以高效地制造出气密性稳定的支撑圈间隔腔体。
【技术特征摘要】
1.一种适用于流动床炼化装置双层筒状内件设备的激光焊接方法,其特征在于:所述方法将网筒中截面为三角形的网丝(1)垂直于支撑圈(2)的径向方向连接至支撑圈(2)上形成交错的网状结构,网丝(1)的一角与支撑圈(2)上的齿槽啮合并激光焊接形成整体;然后通过激光透射焊使外层孔板筒(3)与内层网筒成为一体;可以高效地制造出气密性稳定的支撑圈间隔腔体。2.根据权利要求1所述的适用于流动床炼化装置双层筒状内件设备的激光焊接方法,其特征在于:所述焊接工艺方法的具体步骤如下:、采用三阶梯专业拉丝模挤压拉拔的方式,得到符合行业应用规格的三角形截面的网丝(1);同时,利用激光束聚焦切割方法,在支撑圈(2)内环面制备出与三角形截面的网丝(1)的一角啮合的内牙V形齿槽,得到与网丝相啮合的齿形支撑圈(2);、支撑圈(2)上开有定位孔,将支撑杆(5)穿过支撑圈(2)的定位孔,在各支撑杆上嵌入设计尺寸要求的定位套,定位套支撑于两个相邻的支撑圈(2)之间,使得两个相邻的支撑圈(2)的距离固定,将以上工序循环操作至内层网筒所需高度;、将三角形截面网丝(1)从上到下依次穿入支撑圈的V型齿槽内,将高能量密度的激光束聚焦到网丝(1)与支撑圈(2)的齿槽之间相结合部位的两侧,使得该部分的网丝(1)与齿槽的金属材质瞬时熔融之后并迅速冷却硬化,将网丝(1)和支撑圈焊接为一体;、待全部网丝与支撑圈上的齿槽啮合并完成焊接以后,形成内层网筒,在内层网筒外围包装外层孔板筒(3),通过调节紧裹工装,使得外层孔板筒(3)紧密贴合在支撑圈(2)外部,在与支撑圈(2)相接触的外层孔板筒(3)外侧进行激光连续透射焊,使外层孔板筒(3)与内层网筒焊为一个整体。3.根据权利要求1所述的适用于流动床炼化装置双层筒状内件设备的激光焊接方法,其特征在于:所述支撑圈为齿槽在内环面的内牙支撑圈,与网丝(1)形成嵌入结构;所述支撑圈(2)的齿槽为V形结构,使得整个支撑圈(2)形成齿形结构,支撑圈(2)是由多段弧形支撑齿条拼接对焊而成。4.根据权利要求1所述的适用于流动床炼化装置双层筒状内件设备的激光焊接方法,其特征在于:③步骤中的激光束为800W-2700W的激光束;“③、④”步骤中激光焊接是利用光纤将激光器产生的激光束导入到可以在三维空间自由运动的激光焊接头,激光焊接头借助六轴联动机械手,经过精确聚焦的高能量激光束沿着网丝(1)和齿槽的啮合部分运动,实现激光焊接;精确聚焦的高能量激光束焦距为:250-300mm;光斑为:0.5-1.2mm。5.根据权利要求1所述的适用于流动床炼化装置双层筒状内件设备的激光焊接方法,其特征在于:所述的定位套包括...
【专利技术属性】
技术研发人员:商硕,
申请(专利权)人:辽宁裕通石化机械仪表有限公司,
类型:发明
国别省市:辽宁,21