一种难选金矿的脱碳脱硫菌剂及其应用制造技术

本发明专利技术属于冶金技术领域，涉及一种难选金矿的脱碳脱硫菌剂，该菌剂由，脂环酸芽孢杆菌、嗜酸氧化亚铁硫杆菌、铜绿假单胞菌、枯草芽孢杆菌、巨大芽孢杆菌、伯克霍尔德氏菌混合而成。本发明专利技术还公开了利用上述菌剂处理难选金矿的方法。本发明专利技术的菌剂可处理含硫量15％以上，含碳8％以上的的高碳高硫金矿，同时氰化提金所需要的氰化钠得以大幅降低，降低了工业成本。

Decarbonization desulfurizing agent for refractory gold ore and its application

The invention belongs to the technical field of metallurgy, relates to a desulfurization and decarbonization agent for refractory gold ores, the bacteria by Alicyclobacillus, Acidithiobacillus ferrooxidans, Pseudomonas aeruginosa, Bacillus subtilis, Bacillus megaterium, Burke Holder's mixture of bacteria. The invention also discloses a method for treating refractory gold ore by using the microbial agent. The bacterial agent of the invention can handle more than 15% sulfur containing carbon and high carbon high sulfur gold ore containing more than 8% of carbon, and simultaneously, the sodium cyanide needed for the cyanidation of gold is greatly reduced, and the industrial cost is reduced.

【技术实现步骤摘要】

本专利技术属于矿产资源选矿领域，涉及一种难选金矿的脱碳脱硫菌剂及其应用。
技术介绍
随着金矿资源的不断开发利用以及黄金生产规模的日益扩大，易处理金矿石资源逐渐枯竭，难处理矿石也将逐步成为企业未来的主要资源。针对许多矿山开采生产的含碳(石墨)含硫型金矿石，由于此矿石中含碳(石墨)或其他形式的碳物质和含硫，若不经过处理直接氰化浸出，在氰化浸出的过程中，这种含碳(石墨)和含硫的物质对金氰络合物具有相当强的吸附活性，一部分金转入溶液的氰化过程中，另一部分金却又被矿石中存在的含碳(石墨)物质所吸附而随尾矿流失，增加了金的损失，也降低了浸出率，这样这类矿石就给氰化提金工艺带来很大的障碍。目前处理这类难处理金矿主要是采用原矿细磨浮选-金精矿氧化-氰化提金工艺，通过氧化其中的硫化物，解离出包裹的金，然后采用氰化炭浸、氰化炭浆等工艺提金，目前工业应用的氧化方法主要有生物氧化、加压氧化、焙烧氧化。生物氧化存在操作周期长，氧化不彻底，细菌对碳硫等有害离子敏感，金浸出率低等缺点，并且氧化后金精矿中的C元素和S元素等杂质大部分进入溶液中，造成酸性氧化液中和成本高，在处理含碳和含硫的金精矿时不能解决有机碳的“劫金”问题，影响金的浸出。目前，现有技术研究的比较多的是利用铁氧化菌和硫氧化菌组成的混合微生物菌齐 ，它们都是混合作用于难处理金矿物。现有技术的混合菌群主要是将低价硫化合物氧化为可溶性硫酸盐；这类混合菌群既能高效氧`化Fe2+，又能高效氧化硫化物产生硫酸和硫酸盐，但是对碳化物的作用较差。
技术实现思路
为了克服现有技术的不足，本专利技术提供了一种难选金矿的脱碳脱硫菌剂。该方法中各微生物配伍合理，相互协同，能够达到较佳的脱碳脱硫效果，金的浸出率也大大提高，并且能够回收重复利用，环保无污染。本专利技术还公开了一种利用菌剂处理难选金矿的方法。一种难选金矿的脱碳脱硫菌剂，该菌剂由下列重量份的原料混合而成: 脂环酸芽孢杆菌10份、嗜酸氧化亚铁硫杆菌8份、铜绿假单胞菌6份、枯草芽孢杆菌4份、巨大芽孢杆菌4份、伯克霍尔德氏菌3份。所述脂环酸芽孢杆菌优选脂环酸芽孢杆菌Alicyclobacillus，CGMCC4500 (参见CN2011100247602公开使用)，将脂环酸芽孢杆菌的培养基为BAM培养基，30°C培养至活菌数达到1.0X IO8个/克。所述嗜酸氧化亚铁硫杆菌优选嗜酸氧化亚铁硫杆菌AcidithiobaciIIusferrooxidans ATCC 53993(可参见文献 A genomic island provides Acidithiobacillusferrooxidans ATCC 53993 additional copper resistance: a possible competitiveadvantage.Appl Microbiol Biotechnol.2011);所述嗜酸氧化亚铁硫杆菌于9K培养基((NH4) SO4 3g/L, KCl 0.lg/L, K2HPO4 0.5g/L, Ca (NO3) 2 0.0lg/L, FeSO4.7H20 44.43g/L)28-30°C培养至产品中活菌数达到1.0X IO8个/克。所述铜绿假单胞菌优选Pseudomonas aeruginosa, ATCC15442 (例如参见文献Adaptation of Pseudomonas aeruginosa ATCC 15442 to didecyIdimethyIammoniumbromide induces changes in membrane fatty acid composition and in resistanceof cells, Journal of Applied Microbiology, 2001);铜绿假单胞菌首先在培养基上，28-30°C，作一级斜面培养，然后二级种子培养、混合发酵培养至产品中活菌数达到1.0X IO8 个 / 克，所述培养基成分为=NH4 Cl 1.0g, CH3 COONa 3.5g，MgCl 2 0.lg, CaCl20.lg, KH2 PO4 0.6g, K2 HPO4 0.4g，酵母膏 0.lg，水 IOOOmI，ρΗ7.2。所述枯草芽孢杆菌优选为枯草芽孢杆菌subtil is) CGMCC No:0954(CN1554744A)、所述巨大芽孢杆菌优选为巨大芽孢杆菌(Bacillus megatherium) CGMCCNo:2267 (CN101215532A):将所述枯草芽孢杆菌或巨大芽孢杆菌试管种首先接种在牛肉膏蛋白胨培养基上，28-300C，作一级斜面培养，然后接种到三角瓶里做振荡二级液体培养，然后转入液体发酵罐做三级液体培养，最后接种到固体培养基上作四级培养，至产品中活菌数达到2.0-4.0X IO8个/克。所述伯克霍尔德氏菌优选伯克霍尔德氏菌Burkholderia sp, CGMCC N0.3223 (可参见CN101671636A);首先接种在马铃薯葡萄糖琼脂培养基(PDA)上，28_30°C，作一级斜面培养，然后发酵培养至产品中活菌数达到1.0X IO8个/克。将上述培养的菌液按照质量比例10:8:6:4:4:3混合得到菌剂液体；然后与载体搅拌混合，优选以80目的硅藻 土为载体，按照液体菌剂:载体为3:1的重量比混合，然后进行干燥，干燥温度为29°C，干燥后含水量为30%。上述菌液的获得方式仅仅是优选方式，上述步骤中菌种扩大培养的方法不是唯一的，本领域技术人员可以根据常识选择合适的培养基及扩大培养方法，使活菌数达到IO8个/克。本专利技术所述菌种均可以从中国微生物菌种保藏管理委员会普通微生物中心(CGMCC)中国典型培养物保藏中心以及美国模式培养物集存库(ATCC)购买得到。本专利技术还公开了一种利用上述菌剂处理难选金矿的方法，其包括如下步骤: 将难选金矿经过碎矿机破碎，然后送至球磨机，磨至粒径为100目的矿粉，其中球磨机中添加活化剂，添加量为金矿质量的千分之一；所述活化剂按照硅酸钠:四氯化碳为1:1的质量比混合而成；加水调整成矿粉浓度为30% (w/v)的矿浆液。将上述菌剂投入到矿浆液中，其中菌剂和矿浆液的质量比例为1:150 ;边通入空气边搅拌，搅拌速度为200转/分，在30°C的条件下进行微生物催化，催化时间为5天，其中在第三天时，在矿浆液中添加磷酸铵，其中磷酸铵和矿浆液的质量比例为1:100 ； 催化反应完成后，过滤收集滤液和滤渣，其中所得滤液可用于下一次催化反应；所得滤渣加水调配成固料浓度为30% (w/v)的渣浆，然后用石灰将渣浆酸度调整到11，然后加入氰化钠，氰化钠用量Ikg/吨渣浆，通入空气，在200转/分的搅拌速度下氰化提金，氰化时间为24小时。本专利技术取得的有益效果如下: 1.本专利技术经过多年的研究，经历了大量单因子试验，终于选择出了合适的微生物种类以及配比，使得微生物之间较好的共生，它们之间具有较好的协同作用和优势互补，并且能够有效地能将难选金矿石中的碳化物以及硫化物分解，使微粒金暴露出来，易于氰化提取，大大提高了金的浸出率。2.本专利技术制备的菌剂对高碳高硫的耐受性好，并且能够回收重复利用，节约了资源，避免了环境污染。3.本发本文档来自技高网...

【技术保护点】
一种难选金矿的脱碳脱硫菌剂，该菌剂由下列原料混合而成：脂环酸芽孢杆菌、嗜酸氧化亚铁硫杆菌、铜绿假单胞菌、枯草芽孢杆菌、巨大芽孢杆菌、伯克霍尔德氏菌。