The invention relates to a preparation method of the metal zinc nanometer wire, belonging to the technical field of nanometer material preparation. By DC arc discharge device, ZnO powder, C powder, mixed powder pressed into the pressing block; the pressure block is arranged at the graphite copper pot pot, the anode reaction chamber in the DC arc discharge device in the reaction chamber; filled with argon, copper pot into the circulating cooling water discharge process to maintain voltage; 20 ~ 40V, current is 80 ~ 120A, 5 ~ 10 minutes; repassivation in argon environment, collect the dark grey powder on the graphite pot metal Zn nanowires. The invention has the advantages of simple method, fast reaction, low cost, no pollution, large output, high purity of sample, good repeatability and no need to add catalyst. The prepared products have potential applications in thermoelectric materials, photoelectric materials, magnetoresistance, and other fields.
【技术实现步骤摘要】
本专利技术属于纳米材料制备的
，特别涉及了一种简单的制备金属Si纳米 线的方法。
技术介绍
随着对纳米材料研究的广泛和深入，人们发现纳米材料具有大的比表面积，表面 原子数、表面能和表面张力随粒径的下降急剧增加，表现出小尺寸效应、表面效应、量子尺 寸效应及宏观量子隧道效应等特点，从而导致纳米材料的熔点，磁学性能，电学性能，光学 性能，力学性能等都不同于传统材料。一维纳米结构材料如纳米管、纳米线、纳米棒、纳米 带、纳米纤维等，由于其独特的光学、电学、磁学、催化性质，在可再生燃料电池，光电子传感 器件等方面有着广阔的应用前景，所以开发一维纳米材料新的合成方法，开发新的性能具 有重大的意义。在金属纳米材料家族中，金属Si的纳米材料一直都是研究的热点，现在有关金属 Si的一维纳米材料主要有锌纳米管，锌纳米线，锌纳米带等。金属Si纳米材料可以通过多 种方法制备，如热分解(Y. W. Wang, L. D. Zhang, G. W. Meng, C. H. Liang, G. Ζ. Wang, S. H. Sun, Chem. Commun. 24 (2001) 263...
【技术保护点】
１．一种金属锌纳米线的制备方法，有如下步骤：将ＺｎＯ粉、Ｃ粉按摩尔比１∶１比例混合均匀，压成密度为０．１４～１．３ｇ／ｃｍ３的混合粉的压块；将压块置于石墨锅内，放入直流电弧放电装置的反应室内的铜锅阳极中，钨棒阴极与铜锅阳极相对放置；将反应室抽成真空后充入氩气，氩气气压为５～２５ｋＰａ，铜锅通入循环冷却水；在放电过程中，保持电压为２０～４０Ｖ，电流为８０～１２０Ａ，反应５～１０分钟；再在氩气环境中钝化，在石墨锅中收集暗灰色的粉末为金属Ｚｎ纳米线。
【技术特征摘要】
【专利技术属性】
技术研发人员：崔啟良，丛日东，王秋实，贾岩，徐永生，王静姝，尹广超，马春丽，
申请(专利权)人：吉林大学，
类型：发明
国别省市：82