The invention discloses a heat treatment process of a piston of a DTH hammer, relating to the heat treatment technology of metal materials. The objective is to select the ideal piston material and treat it with a new heat treatment process to improve the mechanical performance and service life. The invention uses low carbon alloy steel 12CrNi3 for piston material, pre heat treatment and mechanical processing after carburizing heat treatment, the process is: tempering, carburizing, quenching, tempering, sandblasting, cleaning, inspection, carburizing process by three segment, insulation carburizing in three different temperature stages, respectively, to achieve the required parameter index. The invention is used for heat treatment of a piston of a submerged percussion piston. The piston processed by the process can be widely applied to various large driving machines and percussion devices of drilling vehicles.
【技术实现步骤摘要】
本专利技术涉及金属材料的热处理工艺，特别涉及潜孔冲击器活塞的热处理工艺。
技术介绍
潜孔冲击是钻车的凿岩装置，其性能的优劣决定着钻车的工作效率，是整台钻车 的关键部件。而冲击器的性能好坏和使用寿命的长短则取决于活塞的性能，因此，冲击器的 活塞便是整台钻车的关键零件。现在钻车上所装的活塞因其材料选用不当和热处理工艺不 合理，导致活塞性能不佳，使用过程中易产生裂纹以至发生断裂，使用寿命不长，需要不时 换件，直接影响着钻车的工作性能和凿岩效率。
技术实现思路
本专利技术针对现用活塞存在的问题，经试验、研究，提供一种较理想的活塞材料及该 材料所制活塞的热处理工艺，以提高活塞的综合性能和使用寿命。本专利技术采取的技术方案如下经分析、对比，活塞材料选用12CrNi3低碳高合金 钢，其化学成份为:c 0. 12、Si 0. 27、Mn 0. 42、S < 0. 01、P 0. 015、Cr 0. 8、Ni 2. 91 ；活塞 的制造工序为1、备料；2、预先热处理；3、机械加工，将胚料加工成活塞零件；4、热处理；5、最后 加工，所述热处理工序为三段式渗碳热处理工艺，其流程如...
【技术保护点】
１．一种潜孔冲击器活塞的热处理工艺，活塞材料为１２ＣｒＮｉ３低碳高合金钢，将备好的料进行预先热处理，再进行机械加工，对加工好的活塞零件进行热处理，其特征在于所述热处理为三段式渗碳热处理工艺，其工艺流程如下表：表中渗碳工序为三段式：第一段：温度８５０℃ 保温１．５ｈ 碳势０．９第二段：温度９２０℃ 保温１５ｈ 碳势１．０５第三段：温度９４０℃ 保温１０ｈ 碳势０．９热处理工序完成后，活塞零件进入最后加工工序。
【技术特征摘要】
【专利技术属性】
技术研发人员：耿志君，赵存权，王玉奎，靳子文，蔡敏斋，
申请(专利权)人：天水风动机械有限责任公司，
类型：发明
国别省市：62[中国|甘肃]