氧化铁-氧化锌纳米复合材料的制备方法技术

本发明专利技术公开了一种氧化铁-氧化锌纳米复合材料的制备方法，用于解决现有的氧化铁-氧化锌复合纳米材料的制备方法反应时间长的技术问题。技术方案是采用微波辅助水热方法在较低的温度和较短的时间制备了形貌规则结晶度高的氧化铁-氧化锌纳米复合材料，与背景技术所采用的方法相比，制备反应时间由24h降低到0.5～1h，时间缩短了20多倍，同时光催性能提高了3.5倍。

Method for preparing iron oxide Zinc Oxide nano composite material

The invention discloses a preparation method of an iron oxide Zinc Oxide nanometer composite material, which is used for solving the technical problem that the preparation process of the existing iron oxide Zinc Oxide composite nanometer material has long reaction time. The technical scheme is in low temperature and short preparation time of the morphology crystalline iron oxide nano composite material of high - Zinc Oxide by microwave assisted hydrothermal method, compared with background technology adopted, the preparation of the reaction time decreased from 24h to 0.5 ~ 1H, shorten the time of 20 times, at the same time light catalytic performance increased by 3.5 times.

【技术实现步骤摘要】

本专利涉及一种纳米复合材料的制备方法，特别是一种氧化铁-氧化锌纳米复合 材料的制备方法。
技术介绍
氧化铁是一种常见而且用途广泛且禁带宽度窄的金属氧化半导体，在光催化、气 体传感器、催化剂以及染料等方面有广泛的应用。但是作为一类非常重要的金属氧化物半 导体，在光催化方面性能并不理想，因此为了提高其光催化性能，使其与其它半导体材料复 合形成核壳结构成为一个有效的途径。目前，由于二氧化钛以及氧化锌的禁带宽度比较大， 制约了对光的利用率，只能在紫外下使用；而氧化铁禁带宽度窄，对光利用率高，但光催化 性差。如果能够用非常有效而且方便的液相方法合成氧化铁和氧化锌纳米复合材料，这种 材料将会成为光催化材料的热选。文 献"Aracely Hernandez, Lourdes Maya, et al. Sol-gel synthesis, characterization and photocatalytic activity of mixed oxide Zn0-Fe203, Journal of sol-gel science and technology，42 (2007)，71-78” 公本文档来自技高网...

【技术保护点】
１．一种氧化铁－氧化锌纳米复合材料的制备方法，其特征在于包括下述步骤：（ａ）按照摩尔量比例２∶１～４∶１称量氧化铁纳米粉体和硝酸锌前驱体，氧化铁和硝酸锌的总摩尔量与去离子水体积的比例ｍｏｌ／Ｌ是１∶６～１∶１１，然后超声形成悬浮液；（ｂ）在悬浮液中加入氢氧化钠，其摩尔量与悬浮液体积比例ｍｏｌ／Ｌ是１∶４～１∶１０，并保持搅拌，然后将混合溶液加入反应容器中，旋紧反应容器，装入微波反应仪中，以１８～２２℃／ｍｉｎ的升温速率加热至１６０～１８０℃，保温０．５～１ｈ；（ｃ）待温度降至室温后，将反应容器中的溶液倒出，再用去离子水反复洗涤过滤，直至过滤后的去离子水的ｐＨ值为中性；（ｄ）将步骤（ｃ）所得到的...

【技术特征摘要】

【专利技术属性】
技术研发人员：晏韦，樊慧庆，
申请(专利权)人：西北工业大学，
类型：发明
国别省市：87