A surface decarburization of WC-Co gradient cemented carbide preform preparation process, is a conventional WC-Co hard alloy compacts dewaxing sintering, soaked in ammonium metatungstate solution, drying after sintering in a vacuum furnace, WC-Co gradient cemented carbide preform prepared surface decarbonization. This process first normal WC-Co hard alloy compacts were obtained pre sintering dewaxing, certain strength and porosity of the pre sintered compact; adding ammonium metatungstate solution, from the surface to form a certain depth and concentration gradient distribution of ammonium metatungstate; after drying the specimen is put in a vacuum furnace for sintering temperature, slow in low temperature stage, make the ammonium metawolframate decomposition, decomposition products (tungsten oxide) and the effect of surface WC, Co, WC-Co to obtain the decarburized surface gradient cemented carbide preform. The preparation method of the invention is simple and convenient to operate, and the WC-Co gradient hard alloy preform with only surface decarburization is prepared, which provides the possibility for improving the comprehensive property of the cemented carbide and is suitable for industrial production.
【技术实现步骤摘要】
本专利技术公开了一种表层脱碳WC-C0梯度硬质合金预制体的制备工艺。属于硬质合 金材料制造
技术介绍
硬质合金是一种以难熔金属化合物(WC、TaC, TiC、NbC等)为基体，以过渡族金属 (&)、狗和附)为粘结相，采用粉末冶金方法制备的金属陶瓷工具材料。由于其高强度、高 硬度、高弹性模量、耐磨损、耐腐蚀、热膨胀系数小以及化学性质稳定等优点，在金属切削、 木材加工、石油矿山钻探、复合材料加工等方面有着重要的应用。常规WC-Co类硬质合金由 WC相和粘结相的两相均勻组成，其产品内外结构及机械性能是一致的，存在着高硬度和耐 磨性与强韧性之间的矛盾。而对于钻头及切割刀具用硬质合金产品在使用时要求表面具有 很高的硬度和耐磨性；但为了使其能承受较大的冲击力并阻止表面产生的裂纹向内扩展， 故又要求硬质合金体内具有较高的韧性。若能克服这一矛盾，制备表面高硬耐磨、心部强韧这种性能呈梯度变化的硬质合 金，将能大大改善硬质合金的使用寿命。二十世纪八十年代，瑞典Sandvik公司开发了此类 功能WC-Co梯度结构硬质合金，成功推出牌号为DP55、DP60和DP65三...
【技术保护点】
１．一种表层脱碳ＷＣ－Ｃｏ梯度硬质合金预制体的制备工艺，包括下述步骤：第一步：正常ＷＣ－Ｃｏ硬质合金压坯脱蜡预烧将正常ＷＣ－Ｃｏ硬质合金压坯在真空条件下于１００～５００℃之间进行脱蜡，然后于８００～９００℃之间进行预烧，获得一定强度及孔隙度的预烧坯；第二步：预烧坯渗钨将第一步所得预烧坯浸泡在偏钨酸铵溶液中，然后在真空条件下进行干燥；第三步：渗钨预烧坯干燥后烧结将第二步所得渗钨预烧坯在真空条件下进行烧结，随炉冷却，即制得表层脱碳ＷＣ－Ｃｏ梯度硬质合金预制体。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。