The invention relates to a method for preparing tungsten fluoride Co doped anatase nanometer titanium dioxide composite powder. Method for preparing tungsten fluoride Co doped anatase nano titanium dioxide composite powder, which is characterized in that it comprises the following steps: 1) by butyl titanate anhydrous ethanol: acetic acid:: HF: Deionized water, ammonium tungstate ratio is 20mL: 200mL: 5mL: 0.15mL: 5mL: 0.1 ~ 85 ~ 340mg, the first selection; anhydrous ethanol and acetic acid mixed stir, mixed liquid; the butyl titanate drops into the mixed liquor, be light yellow sol; 2) preparation of tungsten fluoride solution; 3) will join F-W-H2O drops of light yellow sol, sol was milky white, placed 2 to 3 days; 4) will be placed in 2 ~ 3 after the white sol with deionized water cleaning to pH = 7, after filtration obtained precipitate; drying, by fluorine Co doped anatase TiO2 tungsten composite powder. The invention has the characteristics of low cost and simple preparation process, and can realize batch production and has high catalytic activity and so on.
【技术实现步骤摘要】
本专利技术涉及一种。
技术介绍
TiO2作为耐久的光催化剂已被广泛应用于处理各种污水，其降解对象涉及酚类、 染料等多种有机化合物和部分无机物。Harada Keni等(K. Harada，et al. Water Res., 24(1990) 1415-1417.)对水中34种有机污染物的光催化降解进行了系统的研究，表明光催 化可将水中的烃类、卤代物、表面活性剂、染料、含氮有机物和含磷杀虫剂等较快地完全氧 化为C02、H2O等无害物质。另外，纳米二氧化钛光催化剂在处理无机污染物、空气净化方面 和抗菌方面都有应用。随着纳米二氧化钛在可见光下的催化能力不断被人们开发和利用， 抗菌光灯、抗菌纤维、抗菌建材、抗菌涂料和抗菌陶瓷卫生设施的相继出现，随着科学技术 的发展纳米二氧化钛将会得到更加广泛的应用。然而TiA在实际应用还存在一些亟待解决的问题(1)纳米TiA的太阳能利用率 较低，由于TiA有其自身的局限性，禁带宽度约为3. &V，激发产生电子-空穴对需要紫外 光或近紫外光，对应的吸收光的阀值为387. 5nm，而紫外线部分仅占5%左右；( 电荷载流 子的复合...
【技术保护点】
１．氟钨共掺杂锐钛矿型纳米二氧化钛复合粉末的制备方法，其特征在于它包括如下步骤：１）按钛酸丁酯∶无水乙醇∶乙酸∶ＨＦ∶去离子水∶钨酸铵的配比＝２０ｍＬ∶２００ｍＬ∶５ｍＬ∶０．１～０．１５ｍＬ∶５ｍＬ∶８５～３４０ｍｇ，选取钛酸丁酯、无水乙醇、乙酸、ＨＦ、去离子水和钨酸铵，备用；先将无水乙醇和乙酸混合后搅匀，得到混合液；取钛酸丁酯滴入上述混合液中，此过程中持续搅拌３０～６０分钟，得到浅黄色溶胶；２）氟钨溶液的配制：先将ＨＦ溶于去离子水中，制成ＨＦ水溶液，然后将钨酸铵溶于上述的ＨＦ水溶液中，搅拌使钨酸铵与ＨＦ水溶液充分反应，记为Ｆ－Ｗ－Ｈ２Ｏ；３）在得到浅黄色溶胶后，将Ｆ－Ｗ...
【技术特征摘要】
【专利技术属性】
技术研发人员：史晓亮，秦海波，章桥新，冯四平，彭美超，祝志伟，王莽，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：83
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。