The invention discloses a high temperature rapid lignite carbonization method, which comprises the following steps: (1) high temperature carbonization kiln: Lignite materials in automatic coal carbonization kiln, preheating time 600-1000 C preheating zone, at the temperature of 1400-1700 DEG C high temperature carbonization, hypoxia 10-15 minutes; (2) anaerobic rapid carbonization cooling: Lignite into lignite carbonization in high temperature water bath cooling device of high temperature carbonization will, in a closed anaerobic environment of water bath cooling to 600 DEG, finally closed in the anaerobic environment of stack cooling to room temperature, the product. The invention also discloses the equipment used by the method, the full-automatic lignite high temperature carbonization shaft kiln and the lignite high temperature carbonization water bath cooling device. The low calorific value lignite prepared by automatic high temperature carbonization of carbonization kiln into high value products, can be used as feedstock for production of activated carbon, organic carbon, fine carbon, carbon powder and other products, improve the utilization rate of lignite.
【技术实现步骤摘要】
本专利技术涉及褐煤加工利用领域，具体是一种褐煤高温快速炭化方法，本专利技术还涉 及该方法所使用的设备。
技术介绍
世界上褐煤资源丰富，但是它的发热量低，含水分特高，直接利用有困难，效率低， 利用率低，一般都经过处理和加工，才能成为广泛利用的产品，例如液化发电、炼焦、制合 成氨等，目前较为先进的褐煤加工处理方法是褐煤烘干法，以美国最先进，采用微波技术烘 干进行处理。在我国，这些褐煤利用技术均由于褐煤自身质量差的原因，受到利用的限制， 造成资源的浪费，在当前能源日益枯竭情况下，充分利用褐煤资源及提高利用率具有积极 的意义。
技术实现思路
本专利技术的目的在于克服褐煤利用率低的缺点，提供一种褐煤高温快速炭化方法， 本专利技术的另一目的是提供该方法使用的设备。本专利技术实现目的所采取的技术方案是一种褐煤高温快速炭化方法，包括以下步 骤(1)窑内高温炭化将褐煤原料置入全自动褐煤高温炭化立窑中，经600-100(TC 预热区后，在1400-1700°C温度下，缺氧高温炭化10-15分钟；(2)无氧快速炭化冷却将高温炭化后的褐煤装入褐煤高温炭化水浴冷却装置， 在封闭无氧环境下水浴...
【技术保护点】
１．一种褐煤高温快速炭化方法，包括以下步骤：（１）窑内高温炭化：将褐煤原料置入全自动褐煤高温炭化立窑中，经６００－１０００℃预热区预热时间后，在１４００－１７００℃温度下，缺氧高温炭化１０－１５分钟；（２）无氧快速炭化冷却：将高温炭化后的褐煤装入褐煤高温炭化水浴冷却装置，在封闭无氧环境下水浴快速冷却至６００℃以下，最后在封闭无氧环境堆放冷却到常温，得产品。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。