精陶质陶瓷坯体及其制备与应用制造技术

本发明专利技术涉及精陶质陶瓷坯体及其制备与应用，本发明专利技术的坯体原料包括下列组分及对应的重量百分比：高铝低收缩低热膨胀的煅烧高岭土３０－５０％；陶瓷废品粉料１０－２０％；石英砂１０－２０％；球粘土２０－４０％。本发明专利技术还进一步公开了一种精陶质陶瓷及其制备。本发明专利技术的精陶质陶瓷可以铸造尺寸大于１０００ｍｍ的产品，而且产品平直规整，不易变形。

Fine ceramic solid body, preparation and application thereof

The present invention relates to the preparation and application of fine pottery and ceramic body, the body material of the invention comprises the following components and the corresponding weight percentage: calcined kaolin with high aluminum and low shrinkage and low thermal expansion of 30 - 50%; 10 - 20% ceramic waste powder; quartz sand 10 - 20%; 20 - 40% ball clay. The invention further discloses a fine ceramic and its preparation. The fine ceramics of the invention can be used for casting products of size larger than 1000mm, and the products are flat and regular and difficult to deform.

【技术实现步骤摘要】

本专利技术属于无机非金属材料生产
，具体涉及精陶质陶瓷坯体及其制备与应用。
技术介绍
陶瓷材料作为三大材料之一，因其良好的耐酸碱性，较高的机械强度，优异的表面硬度及耐高温抗氧化的性能而在各领域得以广泛应用，陶瓷材料在卫浴方面的应用已有近百年的历史，但是主要集中于瓷质方面，而传统瓷质洁具干燥收縮加烧成收縮一般为10 13%，产品在干燥烧成过程极易因温度，颗粒分布，含水率等的分布差异造成收縮应力聚集，而卫浴产品往往具有多曲线转折的内外部结构，这样更容易造成坯体在干燥及烧成过程由于应力集中导致坯体应力集中区域开裂，这也是瓷质卫浴产品最主要的报废缺陷之 中国专利申请91110765. 7记载了一种精陶生产工艺技术，属于陶瓷装饰领域，是一种由高岭土、低温瓷土，特种工艺泥土组成，经混合一球磨一压泥一打浆而成为一种低温泥，经注浆成型后低温一次烧成，用硝基磁漆进行彩绘而成为。但该精陶质陶瓷生产成本高，并且并不适合制作大平面大尺寸的卫浴产品。
技术实现思路
本专利技术的目的之一是提供一种精陶质陶瓷坯体及其制备与应用。本专利技术的技术构思如下在传统瓷质材料的基础上，确保材料可塑性的前提条件下，通过本文档来自技高网...

【技术保护点】
一种精陶质陶瓷坯体，其原料包括下列组分及对应的重量百分比：高铝低收缩低热膨胀的煅烧高岭土３０－５０％陶瓷废品粉料１０－２０％石英砂１０－２０％球粘土２０－４０％。

【技术特征摘要】

【专利技术属性】
技术研发人员：曹琛，
申请(专利权)人：上海美标陶瓷有限公司，
类型：发明
国别省市：31[中国|上海]