Including anti oxidation coating on the surface of molybdenum and molybdenum alloy preparation method, the invention relates to a zirconium matrix: (1) the molybdenum rods of alkali washing, acid washing, washing and drying, the molybdenum rod surface by sandblasting texturing; (2) (a) the barium silicate glass mixture in 1350 to 1480 DEG C melting under 2 ~ 4h, water-cooled, milling, 200 mesh sieve, base glaze; (b) ZrO: 2 mo in glaze of refractory filler, preparation of molybdenum glaze; (c) by organic solvent terpineol and clay preparation of inking oil; (d) the molybdenum glaze and inking oil stir into the glaze coating; (E) coated with glaze coating, drying, and alkali free glass cloth soaked in paint glaze bound surface coating glaze layer in the coating, and then drying up. The method has the advantages of simple method and low cost, and can effectively prevent the oxidation of molybdenum electrodes during the roasting of the kiln.
【技术实现步骤摘要】
本专利技术属钼钼及钼合金表面防氧化涂层的制备领域，特别是涉及一种。
技术介绍
钼熔点较高，具有很好的导电、导热性能，高温强度好，在noo'c左右仍有较高的机械强度和较高的抗侵蚀能力。这些性质使得钼作为电极材料在玻璃熔制行业有着广泛的应用。但是钼电极很容易被氧化，在30(TC时钼会缓慢氧化，生成Mo02，温升至60(TC时，钼发生二次氧化，生成Mo03，极易升华挥发。在钼电极表面涂上一层比较薄的涂层材料，以消除外界气氛与钼基体的接触，从而降低了氧向钼基体的扩散速率，防止了钼电极的氧化，提高了钼电极的使用寿命。常用的钼或钼合金的抗氧化涂层的制备方法有高温火焰喷涂法，化学气相沉积(CVD)、等离子喷涂法和真空或惰性气体渗制法和涂抹法。奥地利攀时公司采用高温火焰喷涂法制备出了 SIBOR抗氧化涂层，它是硼、硅组成的复合材料。采用惰性气体扩散和等离子喷涂法，J. J. Moore制备出了 MoSi2+1.96SiC抗氧化涂层。Edward K. Nyutu采用CVD法制备了 MoSi2+Si02复合抗氧化涂层。这几种制备方法工艺复杂，对设备要求高，周期也较长，从而导致了成...
【技术保护点】
一种氧化锆基质的钼及钼合金表面防氧化涂层的制备方法，包括： （１）将钼棒进行弱碱洗、弱酸洗、水洗和烘干，钼棒表面经喷砂毛化； （２）（ａ）将钡硅酸盐玻璃料即组分质量百分比为ＳｉＯ↓［２］：３６－４０％；ＢａＯ：４０－４５％；Ｂ↓［２］Ｏ↓［３］：５－７％；ＺｎＯ：４－６％；ＣａＯ：３－５％；Ａｌ↓［２］Ｏ↓［３］：０－２％，混合均匀，在１３５０℃～１４８０℃下熔炼２～４ｈ，只要熔化即可，迅速将高温玻璃熔体水冷，再经４８～７２ｈ球磨后，过２００目筛，为基釉； （ｂ）以ＺｒＯ↓［２］为钼釉中的难熔填料，钼釉的质量配比为基釉∶ＺｒＯ↓［２］∶粘土＝１４∶（２～６）∶１； ...
【技术特征摘要】
【专利技术属性】
技术研发人员：汪庆卫，宁伟，关志峰，罗理达，陈健，王智勇，
申请(专利权)人：东华大学，
类型：发明
国别省市：31[中国|上海]