The present invention provides a novel catalyst for catalytic cracking of olefins to produce propylene and ethylene, and a method for using the same. The catalyst of the present invention of Si / Al ratio SiO: 2 / Al: 2 O: 3 to 10 - 300, the grain size is 10 - 800 of the phosphorus nanometer molecular sieve ZSM 5 and loaded on the and rare earth metal elements. The catalyst applied to carbon four carbon twelve olefins as raw materials, the reaction temperature is 450 to 650 DEG C, the reaction pressure is 0 0.3MPa, speed is 1 - 14 weight olefins, 1 - hour increase, water / olefin to weight ratio of 0.1 - 10 under the condition of raw materials for olefin catalytic cracking the reaction of propylene and ethylene through the catalyst bed. The catalyst provided by the invention can keep the high yield of propylene and ethylene at the same time and has a longer reaction running time and can be used for industrial production.
【技术实现步骤摘要】
本专利技术涉及一种催化裂解生产丙烯、乙烯的催化剂及其应用，特别涉及一种用于碳四 碳十二烯烃催化裂解生产丙烯、乙烯的催化剂及其应用。
技术介绍
据统计，1995年世界乙烯生产能力为7932万吨/年，预计至2010年则为11038万吨/年。随着乙烯产量的增加，蒸汽裂解的副产碳四及碳四以上烯烃的产量不断增加，受化工产品市场的变化以及运输成本等因素的影响，对这些低附加值物料进行就地深加工是一种较好的利用途径。同时，受聚丙烯以及烷基芳烃化合物需求增长的影响，丙烯需求增长旺盛，到2008年丙烯需求量将达到7800万吨。分析家指出，如果不设法增加丙烯产量，到2010丙烯的缺口将达到500万吨/年，因此，在今后一段时期内，丙烯被认为是具有很大市场潜力的产品。针对上述情况，世界上许多石化公司纷纷投入力量来开发利用碳四及碳四以上低值烯烃生产丙烯的工艺及催化剂。CN1284109A公开了一种用于碳四以上烯烃裂解制丙烯、乙烯的工艺，反应系统中不添加水，反应空速为10 — 30小时—'，其所用的催化剂为一种硅铝摩尔比大于200的水热改性ZSM-5分子筛，其实施例3中醚化碳四裂解转化率为5...
【技术保护点】
一种用于烯烃催化裂解生产丙烯和乙烯的催化剂，其由以下组分组成： ａ）４０－７５％的硅铝摩尔比ＳｉＯ↓［２］／Ａｌ↓［２］Ｏ↓［３］为１０－３００、晶粒粒径为１０－８００纳米的ＺＳＭ－５分子筛；和载于其上的 ｂ）０．０１－１０％的 磷元素； ｃ）０．０１－１０％的稀土金属元素； ｄ）５－６０％的粘结剂； 其中所述的百分含量均为重量百分含量，且以催化剂总重计。
【技术特征摘要】
【专利技术属性】
技术研发人员：白杰，郝雪松，刘小波，王超，陈硕，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司北京化工研究院，
类型：发明
国别省市：11[中国|北京]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。