The invention provides a fast vulcanizing NBR formula, the weight of the formula material is 100 parts of NBR, 4 parts of zinc oxide, 1 part of stearic acid, 5 parts of antioxidant, 55 parts of quick pressing carbon black, 15 parts of dioctyl ester, 1 part of sulfur and 6.5 parts of accelerator. The butyl rubber is made by the mass proportion of acrylic rubber, zinc oxide, stearic acid, antioxidant, quick pressing carbon black, dioctyl grease, sulfur and accelerator. The vulcanization speed of NBR is improved by the optimization of accelerator proportion, so the production efficiency can be greatly improved. In addition, flame retardant is added to improve the fire resistance of rubber, wear-resistant agent is added to enhance the high wear resistance of rubber and reinforcing agent and plasticizer are added to improve the strength of rubber.
【技术实现步骤摘要】
一种快速硫化丁腈橡胶配方
本专利技术涉及橡胶
,尤其涉及一种快速硫化丁腈橡胶配方。
技术介绍
现有橡胶生产中需要进行硫化。然而现有的丁腈橡胶硫化曲线平坦,硫化速度较慢,从而会导致生产效率的降低。因此,解决这一类的问题显得尤为重要。
技术实现思路
针对上述问题,本专利技术提供一种快速硫化丁腈橡胶配方,通过将丁腈胶、氧化锌、硬脂酸、防老剂、快压出炭黑、二辛脂、硫磺和促进剂的质量份数配比,制造丁基橡胶,通过促进剂比例的优化,来提高丁腈橡胶硫化速度,从而能够大幅提高生产效率。为解决上述问题,本专利技术提供一种快速硫化丁腈橡胶配方,所述配方材料的质量份数为丁腈胶80-120份,氧化锌3-5份,硬脂酸0.5-1.5份,防老剂4-6份,快压出炭黑45-65份,二辛脂10-20份,硫磺0.5-1.5份,促进剂5.5-7.5份。进一步改进在于:所述配方材料的质量份数为丁腈胶100份,氧化锌4份,硬脂酸1份,防老剂5份,快压出炭黑55份,二辛脂15份,硫磺1份,促进剂6.5份。进一步改进在于:所述配方中还添加有增塑剂5-7份,所述增塑剂采用环保醚类增塑剂。进一步改进在于:所述配方中还添加有阻燃剂55-65份。进一步改进在于:所述配方中还添加有耐磨剂1-3份。进一步改进在于:所述配方中还添加有补强剂3-5份。本专利技术的有益效果:通过将丁腈胶、氧化锌、硬脂酸、防老剂、快压出炭黑、二辛脂、硫磺和促进剂的质量份数配比,制造丁基橡胶,通过促进剂比例的优化,提高丁腈 ...
【技术保护点】
1.一种快速硫化丁腈橡胶配方,其特征在于:所述配方材料的质量份数为丁腈胶80-120份,氧化锌3-5份,硬脂酸0.5-1.5份,防老剂4-6份,快压出炭黑45-65份,二辛脂10-20份,硫磺0.5-1.5份,促进剂5.5-7.5份。/n
【技术特征摘要】
1.一种快速硫化丁腈橡胶配方,其特征在于:所述配方材料的质量份数为丁腈胶80-120份,氧化锌3-5份,硬脂酸0.5-1.5份,防老剂4-6份,快压出炭黑45-65份,二辛脂10-20份,硫磺0.5-1.5份,促进剂5.5-7.5份。
2.如权利要求1所述的一种快速硫化丁腈橡胶配方,其特征在于:所述配方材料的质量份数为丁腈胶100份,氧化锌4份,硬脂酸1份,防老剂5份,快压出炭黑55份,二辛脂15份,硫磺1份,促进剂6.5份。
3...
【专利技术属性】
技术研发人员:朱秀祥,吕晓刚,吴喜林,王化勇,
申请(专利权)人:芜湖集拓橡胶技术有限公司,
类型:发明
国别省市:安徽;34